在树脂基复合材料的成型工艺中大多涉及到树脂的流动过程,而树脂压力是反映这一过程的重要参数,监测成型过程中树脂压力的变化可以为工艺参数的选择和构件质量的控制提供指导.本文中针对热压工艺,根据液体传压原理和特点,自行研制了复合材料成型过程树脂压力测试系统,对系统的精度和动态响应性能进行了研究,并以该系统为测试手段,初步研究了玻璃纤维单向层板中树脂压力的变化规律.结果表明,该系统具有准确度高和动态响应敏感的特点,满足热压成型过程树脂压力的测试要求,为研究工艺过程树脂流动行为提供了有力的测试与验证手段.
参考文献
| [1] | Costa V A F,Sousa A C M.Modeling of flow and thermokinetics during the cure of thick laminated composites[J].International Journal of Thermal Sciences,2003,42:15-22. |
| [2] | Frank-Susich D.Cure cycle simulation for thermoset composites[J].Comp Manu,1993,4(3):139-146. |
| [3] | 秦伟,李海晨,张志谦,等.RTM工艺树脂流动过程数值模拟及实验比较[J].复合材料学报,2003,20(4):77-80.Qin Wei,Li Haichen,Zhang Zhiqian,et al.Comparison between numerical simulation and experimental result of resin flow in RTM[J].Acta Materiae Compositae Sinica,2003,20(4):77-80. |
| [4] | 戴福洪,张博明,杜善义,等.复杂形状三维薄壁构件RTM制造工艺注模过程模拟[J].复合材料学报,2004,21(2):87-91.Dai Fuhong,Zhang Boming,Du Shanyi,et al.Simulation of mould-filling in RTM process for 3D complex shape thin shell parts[J].Acta Materiae Compositae Sinica,2004,21(2):87-91. |
| [5] | Gutowski T G,Cai Z,Bauer S,et al.Consolidation experiments for laminate composites[J].J Comp Mater,1987,21(7):650-669. |
| [6] | 杨滔,阿茹娜,张佐光,等.树脂基复合材料模压成型用BH315-3D温度场采集系统[J].玻璃钢/复合材料,2003(3):27-33.Yang Tao,Zhamu Aruna,Zhang Zuoguang,et al.BH315-3D temperature field collection system used in press molding process of thermosetting resin matrix composites[J].Fiber Reinforced Plastics/Composites,2003(3):27-33. |
| [7] | Gutowski T G,Morigaki T,Cai Z.The consolidation of laminate composites[J].J Comp Mater,1987,21(2):172-188. |
| [8] | Dave R.A unified approach to modeling resin flow during composite processing[J].J Comp Mate,1990,24(1):22-41. |
| [9] | Pascal H,Anoush P.A review of flow and compaction modeling relevant to thermoset matrix laminate processing[J].Journal of Reinforced Plastics and Composites,1998,17 (4):286-318. |
| [10] | 顾轶卓,张佐光,刘洪新,等.热压工艺中单向预浸料压缩特性的实验研究[C]//中国航空学会第5届复合材料专业委员会航空用复合材料新技术及其应用研讨会论文集.北京:中国航空学会,2005:97-103. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%