利用Hopkinson杆加载装置,对带有单边切口的炭纤维增强复合材料(CFRP)及玻璃纤维增强复合材料(GFRP)层板试件进行冲击拉伸加载实验.根据一维应力波理论求得作用于试件上的载荷P(t)和试件加载点的位移δ(t).根据试样中应力随时间的变化历史σ(t),并基于断裂韧性测试原理,建立了动态应力强度因子K1(t)响应曲线.利用柔度变化率方法确定起裂时间,分别得到在两种加载速率下CFRP、GFRP层板的动态断裂韧性.结果表明,随着加载速率的提高,这两种复合材料的断裂韧性降低.
参考文献
[1] | 陈锡花,唐国翌,阎允杰,等.炭纤维/环氧树脂复合材料在爆炸冲击下的微损伤分析[J].清华大学学报,2000,5(40):114-117.Chen Xihua,Tang Guoyi,Yan Yunjie,et al.Damage in carbon fiber/epoxy resin composites under explosive impact[J].Journal of Tsinghua University,2000,5(40):114-117. |
[2] | Wei Jiang,Tsang F F Y,Tjong S C.Loading rate dependence of mode Ⅱ fracture behavior in interleaved carbon fiber/epoxy composite laminated[J].Appl Comp Mater,2001,8(3):361-369. |
[3] | Choi N S.Rate effects on the delamination fracture of multidirectional carbon fiber/epoxy composites under mode Ⅰ loading[J].J Mater Sci,2001,36(12):2257-2270. |
[4] | 刘凯欣,刘维甫,张晋香,等.纤维增强复合材料板中裂纹的动态扩展[J].科学通报,2005,56(4):317-320.Liu Kaixin,Liu Weipu,Zhang Jinxiang,et al.Dynamic expand of the crack in fiber strengthening composite[J].Science Bulletin,2005,56(4):317-320. |
[5] | 刘伟华,王鲁,程焕武,等.SiC/Zr基非晶复合材料的动态断裂特性研究[J].兵器材料科学与工程,2005,28(3):14-16.Liu Weihua,Wang Lu,Cheng Huanwu,et al.Dynamic mechanical characteristics of SiC skeleton/Zr based amorphous matrix composites[J].Material Science and Engineering for Weapons,2005,28(3):14-16. |
[6] | 王保林,杜善义,韩杰才,等.非均匀复合材料的动态热弹性断裂力学分析[J].力学学报,1999,31(5):550-554.Wang Baolin,Du Shanyi,Han Jiecai,et al.Dynamic fracture mechanics analysis for non-homogeneous composite material with multiple cracks[J].Acta Mechanica Sinica,1999,31(5):550-554. |
[7] | Stout M G,Koss D A,Liu C,et al.Damage development in carbon/epoxy laminates under quasi-static and dynamic loading[J].Comp Sci Tech,1999,59(14):2339-2350. |
[8] | Ravi S,Iyengar N G R,Kishore N N,et al.Experimental studies on damage growth in composites under dynamic loads[J].ApplComp Mat,2001,8(1):79-97. |
[9] | Goldberg R K,Stouffer D C.Strain rate dependent analysis of a polymer matrix composite utilizing a micromechanics approach[J].J Comp Mater,2002,36(7):773-793. |
[10] | 刘瑞堂,刘文博,刘锦云.工程材料力学性能[M].哈尔滨:哈尔滨工业大学出版社,2001:263. |
[11] | 陆毅中.工程断裂力学[M].西安:西安交通大学出版社,1987:35. |
[12] | 范天佑.断裂理论基础[M].北京:科学出版社,2003:282. |
[13] | Harris C E,Morris D H.A comparison of the fracture behavior of thick laminated composites utilizing compact tension,three-point bend,and center-cracked tension specimens[J].Fracture Mechanics:ASTM STP 905,1986,17(1):124-135. |
[14] | Shan Khan M Z,Simpson G,Gellet E P.Resistance of glassfiber reinforced polymer composites to increasing compressive strain rates and loading rates[J].Composites Part A,2000,31(1):57-67. |
[15] | Takashi Y,Keizo K,Motohiro N.Evaluation of dynamic fracture initiation toughness using a novel impact bend test procedure[J].J Society of Mater Sci,1990,39(447):1637-1643. |
[16] | Kobayashi T,Yamamoto I,Niinomi M.Evaluation of dynamic fracture toughness parameters by instrumented charpy impact test[J].Eng Fracture Mech,1986,24(3):773-782. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%