基于时间增量原理,推导了层合板接头疲劳加载累积损伤应力-应变分析的虚功方程.同时,引入Hashin三维疲劳失效准则进行材料的损伤判定,并结合建立的疲劳加载材料退化模型、4种基本损伤机制相互关联作用的材料性能退化方法及复合材料接头最终失效判据,建立了层合板接头疲劳载荷作用下三维累积损伤分析的寿命预测方法.最后,对层合板接头拉-拉疲劳载荷作用下的损伤累积扩展与失效规律进行了仿真分析,并与试验结果进行了对比,结果表明:本文中建立的寿命预测方法能够很好地预测层合板接头的寿命以及损伤发生、扩展及最终失效.
参考文献
| [1] | 王丹勇,温卫东,崔海涛.复合材料单钉接头三维逐渐损伤破坏分析[J].复合材料学报,2005,22(3):168-174.Wang Danyong,Wen Weidong,Cui Haitao.Three-dimen-sional progressive damage analysis of single fastener joints in composite laminates[J].Acta Materiae Compositae Sinica,2005,22(3):168-174. |
| [2] | 王丹勇,温卫东,崔海涛.含材料非线性的复合材料单钉接头累积损伤分析[J].固体力学学报,2006,27(2):186-190.Wang Danyong,Wen Weidong,Cui Haitao.Progressive dam-age analysis considering the material nonlinearity of composite laminates containing a hole[J].Acta Mechanics Solida Sinica,2006,27(2):185-190. |
| [3] | Tserpes K I,Labeas G,Papanikos P,Kermanidis T.Strength prediction of bolted joints in graphite/epoxy composite lami-nates[J].Composites Part B,2002,33(7):521-529 |
| [4] | Riccio A,Scaramuzzino F.Influence of damage onset and propagation on the tensile structural behavior of protruding composite joints[C]//4th GRACM Congress on Computation Mechanics GRACM 2002.Greece,2002:1-15. |
| [5] | Counts W A,Johnson W S.Bolt bearing fatigue of polymer matrix composites at elevated temperature[J].International Journal of Fatigue,2002,24(2):197-204. |
| [6] | Starikov R,Schon J.Experimental study on fatigue resistance of composite joints with protruding head bolts[J].Composite Structure,2002,55(1):1-11. |
| [7] | Chen H S.The static and fatigue strength of bolted joints in composites with hygrothermal cycling[J].Composites Struc-tures,2001,52(3):295-306. |
| [8] | Schütz D,Gerharz J J,Alschweig E.Fatigue properties of un-notched,notched,and jointed specimens of a graphite/epoxy composite[M]// Fatigue of Fibrous Composite Materials.Philadelphia,PA:ASTM,1981:31-47. |
| [9] | Iorio A D,Lecce L,Mignosi S.Fatigue damage evaluation in multifastened CFRP joints[C]// Vallari S R,Taplin D M R,eds.Advances in Fracture Research.New Delhi:Pergamon Press,1984:3045-3051. |
| [10] | 张开达,石彩华.复合材料机械联接接头的寿命估算[J].机械科学与技术,1996,15(6):897-902.Zhang Kaida,Shi Caihua.Prediction of fatigue life for me-chanical joint in laminated composites[J].Mechanical Science and Technology,1996,15(6):897-902. |
| [11] | Shokrich M M,Lessard L B.Progressive fatigue damage modeling of composite materials Ⅰ:Modeling[J].Journal of Composite Materials,2000,34(13):1056-1080. |
| [12] | Shokrieh M M,Lessard L B.Progressive fatigue damage mod-eling of composite materials Ⅱ:Material characterization and model verification[J].Journal of Composite Materials,2000,34(13):1081-1116. |
| [13] | Tserpes K l,Papanikos P,Labeas G,et al.Fatigue damage accumulation and residual strength assessment of CFRP lami-nates[J].Composite Structure,2004,63(2):219-230. |
| [14] | Hashin Z.Failure criteria for unidirectional fiber composites[J].Journal of Applied Mechanics,1980,47(2):329-335. |
| [15] | 王丹勇.层合板接头损伤失效与疲劳寿命研究[D].南京:南京航空航天大学,2006. |
| [16] | 王丹勇,温卫东.复合材料单向层合板损伤失效试验研究[J].复合材料学报,2007,25(5):142-148.Wang Danyong,Wen Weidong.Experimental research on damage failure of unidirectional laminas[J].Acta Materiae Compositae Sinica,2007,24(5):142-148. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%