以FeSO4·7H2O和NiSO4·7H2O为原料,先制备颗粒细小的碱式碳酸盐前驱体,在300～700℃焙烧1h后,制备出铁酸镍纳米晶,粒度均匀,粒径为8～54nm.用非共线磁结构理论解释了铁酸镍纳米晶的比饱和磁化强度σs与比表面积Sa之间的经验关系式σs(Sa)=σs(∞)(1-aSa),得到纳米晶的非共线表面层的厚度.
参考文献
| [1] | R.Birringer, U.Herrand, H.Gleiter, Suppl. Trans. Jap. Inst., 27(1), 43(1986) |
| [2] | R.Birringer, Phys. Lett., 102A, 524(1984) |
| [3] | 黄波,固体材料及应用(广州,华南理工大学出版社,1995)p.182 |
| [4] | 陈德顺,丘其青,熊茂仁,华南理工大学学报(自然科学版),24(3),111(1996) |
| [5] | H.Tamura, E.Matijevic, J.Colloid Interface Sci., 26(1), 62(1988) |
| [6] | S.Komarneni, E.Fresnius, W.Ebreval, R.Roy, J.Am. Ceram. Sco., 71(1), 26(1988) |
| [7] | A.H.Morrish, K.Haneda, J.Magn. Magn. Mater., 35, 105(1983) |
| [8] | D.Lin, A.A.Nunes, C.F.Majkrzak, A.E.Berkowitz, J.Magn. Magn. Mater., 145, 343(1995) |
| [9] | R.H.Kodama, A.E.Berkowitz, E.J.McNiff. Jr, S.Foner, Phys. Rev. Lett., 77, 394(1996) |
| [10] | P. Kishan, M.B.Madsen, C.J.W.Koch, Indian J. Pure Appl. Phys., 19, 83(1981) |
| [11] | P. Mollard, P.Germi, A.Rousset, Physica B, 86, 1393(1977) |
| [12] | K.Haneda, A.H.Morrish, J.Appl. Phys., 63(8), 4258(1988) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%