利用Monte Carlo法计算bcc二元合金在低温下的微观结构,计算中原子交换能满足e1<0和e2<0.对于合金A-50B,e2/e1<2/3和e2/e1>2/3的情形分别对应完整的B2和B32结构.而对于合金A-25B,e2/e1<0.6时,用Monte Carlo方法不易得到完整的D03结构,且B2有序化过程早于D03结构.
参考文献
[1] | P.S.Rudman, Acta Metallurgica, 8, 321(1960) |
[2] | C.R.Houska, J.Phys. Chem. Solids, 24, 95(1963) |
[3] | Burkhard Dunweg, Kurt Binder, Physical Review, 36B, 6935(1987) |
[4] | K.Yaldram, V.Pierron-Bohnes, M.C.Cadeville, M.A.Khan, J.Mater. Res., 10, 591(1995) |
[5] | E.Kentzinger, M.Zemirli, V.Pierron-Bohnes, M.C.Cadeville, H.Bouzar, M.Benakki, M.A.Khan, Materials Science and Engineering, A239~240, 784(1997) |
[6] | Y.Saito, H.Harada, Materials Science and Engineering, 223A, 1(1997) |
[7] | Y.Saito, Materials Science and Engineering, 223A, 10(1997) |
[8] | K.Kawasaki, Phys. Rev., 145, 224(1966) |
[9] | 翁军,朱逢吾,王文东,职任涛,张得志,肖纪美,金属学报,32,1154(1996) |
[10] | H.J.McQueen, G.C.Kuczynski, Transactions of the Metallurgical Society of AIME, 215, 619(1959) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%