研究了氮气压力对自蔓延高温合成AlN的影响和后烧机理.结果表明,自蔓延高温合成AlN的生长机制为气相-晶体(Vapor-Crystal,VC)机制.气相沉积的台阶平面为AlN的基面({0001)面).为了降低表面能,生长台阶必须以六棱柱形态形核.在后烧阶段,AlN颗粒中心的小台阶被重新"蒸发",并沉积到远离中心的大台阶上,使AlN颗粒棱角分明,形状规则.随着氮气压力的增加,燃烧温度逐渐提高,后烧的时间缩短.
参考文献
| [1] | K.Watari, H.J.Hwang, M.Toriyama, S.Kanzaki, J. Am. Ceram. Soc., 79(7), 1979(1996) |
| [2] | Y.Baik, R.A.L.Drew, Key Eng. Mater, 122, 553(1996) |
| [3] | A.W.Weimer, G.A.Cochran, G.A.Eisman, J.P. Henley, B.D.Hook, L.K.Mills, J. Am. Ceram. Soc., 77(1), 3(1996) |
| [4] | A.G.Merzhanov, Combustion and Plasma Synthesis of High-Temperature Materials, edited by. Z.A.Munir,J.B.Holt, (New York, VCH Pubblisher, 1990) p.1 |
| [5] | K.A.Davis, K.Brezinsky, I.Glassman, Combust. Sci. and Tech., 60, 171(1988) |
| [6] | C.C.Agrafiotis, J.A.Puszynski, V.Halvacek, Combust. Sci. and Tech., 76, 187(1991) |
| [7] | O.Kubaschewski,C.B.Alcock著,冶金热化学,邱竹贤,梁英教,李席孟,王介淦译,(北京,冶金工业出版社,1985)p.149 |
| [8] | 江国键,庄汉锐,李文兰,邬凤英,张宝林,无机材料学报,3(4),568(1998) |
| [9] | Z.A.Munir,J.B.Holt,J.Mater.Sci.,22,710(1987) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%