以乙二醇为溶剂,柠檬酸为胶溶剂,用溶胶凝胶法合成La0 8Sr0 2CrO3纳米粉料.结果表明,柠檬酸与乙二醇的重量比为1:1.2,分解温度为800℃时粉料的平均粒径为10～40nm,比表面为98.5～102.5m2/g,在1200℃下即可获得单相钙钛矿结构的La0 8Sr0 2CrO3.在室温与1000℃之间,La0 8Sr0 2CrO3材料电导率的数量级为104～105sm-1.
参考文献
| [1] | W.J.Weber, C.W.Griffin, J.B.Bates, J.Am. Ceram. Soc., 70, 265(1987) |
| [2] | L.Groapp, H.U.Anderson, J.Am. Ceram. Soc., 59, 449-50(1976) |
| [3] | D.P.Karim, A.T.Aldred, Phys. Rev. B:Condens.Matter, 20, 2255(1979) |
| [4] | J.B.Webb, M.Sayer, A.Mansingh, Can. J.Phys., 55, 1725(1977) |
| [5] | S.T.Song, H.Y.Pan, Z.Wang, B.yang, Ceram. Int., 10, 143(1984) |
| [6] | L.Groupp, H.U.Aanderson, J.Am. Ceram. Soc., 59, 449(1976) |
| [7] | 陈广良,刘江,何岚鹰,苏文辉,王斌泰、中国稀土学报,11,131(1993)(CHEN Guangliang, LIU Jiang, HE Lanying, SHU Wenhui, WANG Bintai, Chinese Rare Earth Society, 11,131(1993)) |
| [8] | J.Mixusaki, Y.Mina, S.Yamauchi, K.J.Fueui, Solid.Stat. Chem., 80, 102(1989) |
| [9] | 张源魁,任玉芳,应用化学,10(6),99(1993)(ZHANG Yuankui, REN Yufang, Appl. Chems., 10(6), 99(1993)) |
| [10] | .R.D.Sanchez, J.Mire, J.Rivas, J.Mafer. Res., 14(6), 2533(1999) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%