采用双级雾化和雾滴直接水冷的快速凝固技术制备了(2024A1)-20Si-5Fe合金,利用X射线衍射(XRD)、透射电镜(TEM)等分析测试手段研究了合金的微观组织特征,利用拉伸和磨损实验测定了合金的性能.结果表明:合金具有纳米级的初晶和共晶第二相及沉淀析出相;常温强度为560MPa,473K时的强度为400MPa;滑动摩擦系数比铸造合金低10%,摩擦1500min后的磨损失重为铸造合金的38%.
参考文献
| [1] | M.G.Rodinei, S.Tatsuo, T.Hiroyasu, Akihiko Kamio, Materials Transactions JIM, 39(3), 357(1998) |
| [2] | A.Mocellin, Y.Brechet, R.Fougres, ACTA Metall. Mater., 43(3), 1135(1995) |
| [3] | J.L.Estrada, J.Duszczyk, J.Mater. Sci., 25, 886(1990) |
| [4] | Y.Odani, Y.Takeda, Metal Powder Report, 10, 712(1990) |
| [5] | Y.Wu, W.A.Cssada, E.J.Lavernia, Metall. and Mater.Trans., 23, 1235(1993) |
| [6] | X.G.Yuan, L.Q.Ren, C.S.Cui, D.M.Xu, Q.C.Li, J.Mater. Sci.& Technol., 14(5), 402(1998) |
| [7] | E.J.Lavernia, J.D.Ayers, S.Srivatsan, International Materials Reviews, 37(1), 1～40(1992) |
| [8] | J.Zhou, J.Duszczyk, B.M.Korevaar, J.Mater. Sci., 26, 3041(1991) |
| [9] | O.Masahiro, Y.Harakawa, A.Inoue, T.Masumoto, Mater. Sci. Eng., A181/A182, 1161(1994) |
| [10] | 袁晓光,徐达鸣,李庆春,双级雾化制粉机理及工艺性研究,中国有色金属学报,7(增1),358(1997)(YUAN Xiaoguang, XU Daming, LI Qingchun, The Chinese Journal of Nonferrous Metals, 7(Suppl.1),358(1997)) |
| [11] | 袁晓光,徐达鸣,李庆春,双级雾化快速凝固高硅铝合金粉末形貌及组织特征,金属学报,32(10),1034(1996)(YUAN Xiaoguang, XU Daming, LI Qingchun, Acta Metall. Sin., 32(10), 1034(1996)) |
| [12] | 袁晓光,任露泉,崔成松,徐达鸣,李庆春,快凝A1-Si-Fe-Cu-Mg合金的热稳定相,材料科学与工艺,6(3),7(1998)(YUAN Xiaoguang, REN Luquan, CUI Chengsong, XU Daming, LI Qingchun, Mater. Sci. Technol, 6(3),7(1998)) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%