研究了多相金属间化合物NiAl-33.5Cr-0.5Zr合金的显微组织、高温力学行为与韧脆转变铸造合金由β-NiAl和Q Cr组成的共晶胞及沿共晶胞界分布的Ni2AlZr(Heuskr)相组成.用热等静压处理后,在胞界处的Ni2AlZr相转变为富Zr相该合金具有较高的高温压缩强度,高温压缩变形很好地符合幂指数规律.对高温拉伸延伸率的研究表明,该合金具有较明显的韧脆转变温度(BDTT),当应变速率为1.04×10-4s-1时,韧脆转变温度是1173K,应变速率提高两个数量级时,韧脆转变温度升高约100K.讨论了高温变形和韧脆转变机理.
参考文献
| [1] | D.B.Miracle,Acta.Metall.,41,649(1993) |
| [2] | R.D.Noebe,R.R.Bowman,M.V.Nathak,Inter.Mater.Rev.,38,193(1993) |
| [3] | J.D Whittenberger,R.D.Noebe,S.M.Joslin,B.F.Oliver,Intermetallics,7,627(1999) |
| [4] | D.R.Johnson,X.F.Chen,B.F.Oliver,R.D.Noebe,J.D.Whittenberger,Intermetallics,3,113(1995) |
| [5] | R.S.Polvani,W.S.Tzong,P.S.Strutt,Metallurgical Transactions,7A,33(1976) |
| [6] | R.R.Bowman,R.D.Noebe,S.V.Raj,LElocci,Metallurgical Transaction,23A.1493(1992) |
| [7] | R.Darolia,W.S.Walson,M.V.Nathal,Superalloys,in:R.D.Kisoinger,D.J.Deye,D.L.Anton,(Eds.),The Minerals,Metal and Materials Society,561(1996) |
| [8] | K.Oh-ishi.Z,Nemoto,Mater.Sci.Eng.,A239 ~ 240,477(1997) |
| [9] | R.S.Chen,J.T.Gyo,J.Y.Zhou,Mater.Lett.,42,80(2000) |
| [10] | 杨锐,金属学报,33,107（1997）（YANG Rui,Acta Metallurgica Sinica,33,107(1997)） |
| [11] | E.Cline,J.L.Walter,Metallurgical Transactions,1.2910(1970) |
| [12] | H.Clemens,LRumberg,P.Schretter,P.Grable,O.Lang,A.Wanner and E.Arzt,Mater,Res.Soc.Symp.Proc.,Materials Research Society,288,1087(1993) |
| [13] | J.D.Whittenberger,R.D.Moebe,Metall.Ttans.,27A,2628(1996) |
| [14] | J.D.Whittenberger,J.Mater.Sci.,22,401(1987) |
| [15] | R.D.Noebe,C.L.Cullers,R.R.Bowman,J.Mater.Res.,7,608(1992) |
| [16] | F.Ebrahimi,T.G.Hoyle,Acta.Mater.,45,4193(1997) |