用物理模拟方法研究了铁素体不锈钢EB26-1焊接热影响区HAZ的晶粒长大,通过在不同规范下的等温晶粒长大物理模拟与分析,并结合焊接试验,建立了 HAZ晶粒长大的模型该模型成功地将Arrhenius公式用于热影响区晶粒长大计算,给出了焊接HAZ存在很陡的温度梯度对晶粒长大起阻碍作用的“热钉轧”效应,为选择合适的焊接规范和计算机模拟提供了依据.
参考文献
| [1] | 尹桂全,高甲生,洪永昌,代二国,袁小敏,焊接学报,19,13(1998)(YIN Guiquan, GAO Jiasheng, HONG Yongchang, DAI Erguo, YUAN Xiaomin, Transactions of The China Welding Institution, 19, 13(1998)) |
| [2] | P.A.Manohar, D.P.Dunne, T.Chandra, The Iron and Steel Institute of Japan, 36, 194(1996) |
| [3] | H.A.Drian, F.B.Pickering, Materials Science and Technology, 7, 176(1991) |
| [4] | N.Gao, T.N.Backer, The Iron and Steel Institute of Japan, 38, 744(1998) |
| [5] | N.E.Hannerz, R.Dekazinczy, J.Iron Steel Inst., 208, 475(1970) |
| [6] | M.F.Ashby, K.E.Easterling, Acta Metall., 30, 1969(1978) |
| [7] | H.Hu, B.B.Rath, Metall,Trans., 1, 1381(1970) |
| [8] | R.L.Fullman, Metal Interfaces (Cleveland Ohio, American Society for Metals, 1952) p.179 |
| [9] | F.N.Rhines, K.R.Craig, Metall.Trans., 5, 713(1974) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%