球磨Ni、Al,Ti和 C粉末以合成NiAl-TiC复合材料,分析了反应合成机理结果表明,NiAl和TiC的突然生成归结于两个爆炸反应:Ni+Al→NiAl+△H1,Ti+2C→TiC+△H2.还研究了NiAl和TiC化合物球磨过程中晶粒细化的规律以及粉末颗粒度的变化姚律
参考文献
[1] | R.Darolia, Intermetallics, 8, 1321(2000) |
[2] | 沙宪伟,张修睦,李斌,李依依,材料研究学报,14(2),133(2000)(SHA Xianwei, ZHANG Xiumu, LI Bin, LI Yiyi, Chin. J.Mater. Res., 14(2), 133(2000)) |
[3] | 王瑜,林栋梁,周元鑫,夏源明,C.C.Law,材料研究学报,13(5),464(1999) (WANG Yu, LIN Dongliang, ZHOU Yuanxin, XIA Yuanmin, C.C.Law, Chin. J. Mater. Res., 13(5), 464(1999)) |
[4] | A.Misra, R.Gibala, Intermetallics, 8, 1025(2000) |
[5] | R.Darolia, W.S.Walston, M.V.Nathal, in "Superalloys 1996 ", eds by R.D.Kissinger (TMS, 1996) p.561 |
[6] | C.K.Lin, S.S.Hong, P.Y.Lee, Intermetallics, 8, 1043(2000) |
[7] | J.D.Whittenberger, E.Arzt, M.J.Luton, J.Mater. Res., 5, 271(1990) |
[8] | J.D.Whittenberger, E.Arzt, M.J.Luton, J.Mater. Res., 5, 2819(1990) |
[9] | L.Z.Zhou, J.T.Guo, G.J.Fan, Mater. Sci.& Eng., A249, 103(1998) |
[10] | .I.Barin, O.Knacke, Kwbashewski, Thermochemical Properties of Inorganic Substances (Supplement).(Berlin, Springer-Verlag, 1977) p.18 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%