采用聚醚酰亚胺以提高双酚A二氰酸酯/酚醛环氧树脂共混物的断裂韧性实验结果表明、聚醚酰亚胺是氰酸酯/酚醛环氧树脂共混物的有效增韧剂.加入15%的聚醚酰亚胺可使断裂韧性(Kie)提高到1.45MPa.m0.5,弯曲强度也有所提高.用扫描电子显微镜和动态粘弹谱研究了改性共混物的微观结构.有双连续结构的共混物的耐溶剂性能大大下降.共混物的韧性和耐溶剂性主要与相行为有关,固化工艺对含10%聚醚酰亚胺的共混物的断裂韧性和形态没有明显的作用
参考文献
| [1] | E.Grigat, Kunstst. Plast., 58(12), 827(1968) |
| [2] | D.A.Scola, J.Vontell, Polymer Composites, 8(4), 244(1987) |
| [3] | T.Fang, D.A.Shimp, Prog. Polym. Sci., 20, 61(1995) |
| [4] | I.Hamerton, Chemistry and Technology of Cyanate Ester Resins (Glasgow, Chapman and Hall, 1994) p.l |
| [5] | M.Bauer, W.Tanzer, H.Much, R.Ruhaman, Acta Polym., 40(5), 335(1989) |
| [6] | M.Bauer, J.Bauer, R.Ruhaman, G.Kuhn, Acta Polym., 40(6), 395(1989) |
| [7] | M.Bauer, J.Bauer, Makromol.Chem, Macromol.Symp., 30, 1(1989) |
| [8] | D.A.Shimp, J.H.Wentworth, 37th Int. SAMPE Symp., 37, 293(1992) |
| [9] | R.H.Lin, J.Polym. Sci, Chem. Ed., 38, 2934(2000) |
| [10] | J.W.Hwang, S.D.Park, K.Cho, J.K.Kim, C.E.Park, T.S.Oh, Polymer, 38(8), 1835(1997 |
| [11] | J.W.Hwang, K.Cho, C.E.Park, W.Huh, J.Appl. Polym. Sci., 74(1), 33(1999) |
| [12] | J.W.Hwang, K.Cho, T.H.Yoon, C.E.Park, J.Appl. Polym. Sci., 77(4), 921(2000) |
| [13] | J.Y.Chang, J.L.Hong, Polymer, 41(12), 4513(2000) |
| [14] | S.A.Srinivasan, J.E.McGrath, Polymer, 39(12), 2415(1998) |
| [15] | T.Iijima, S.Katsurayama, W.Fukuda, M.Tomoi, J.Appl. Polym. Sci., 76(2), 208(2000) |
| [16] | I.Harismendy, M.del Rio, A.Eceiza, Gavalda, J.Appl. Polym.Sci., 76(7), 1037(2000) |
| [17] | C.B.Bucknall, A.H.Gilbert, Polymer, 30, 213(1989) |
| [18] | V.A.Pankratov, V.V.Maiorova, V.V.Korshak, S.V.Vinogradova, Vysokomol.Soed., A17, 2189(1975) |
| [19] | D.A.Shimp, J.R.Christenson, S.J.Ising, 34th Int.SAMPE Symp. Exhib., 34(1), 222(1989) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%