研究了应变率对中锰钢的动态拉伸性能的影响.结果表明.在高应变率下中锰钢的室温强度在比低应变率增加近1 倍.塑性由22 8%增加到67. 4%.随着应变率的提高.孪晶数目增加.相应的塑性增加.显著的增塑效应与孪生变形机制有关.也与断裂模式由低应变率的沿晶断裂转化为高应变率的晶内韧窝有关.但不是由相变或绝热温升引起的.
参考文献
[1] | C.H.White. R.W.K.Honeycombe, Journal of The Iron and Steel Institute, 200, 457(1962) |
[2] | W.N.Roberts. Transactions of the Metallurgical Society of AIME. 230. 372(1964) |
[3] | K.S.Raghavan, A.S.Sastri, M.J.Marcinkowski, Trans. of the Metall, Society of AIME. 245, 1569(1969) |
[4] | Y.N.Dastur. W.C.Leslie. Metall. Trans., 12A, 719(1981) |
[5] | P.H.Adler, G.B.Olson, W.S.Owen, Metall. Trans.. 17A, 1725(1986) |
[6] | SHI Deke(石德珂). LIU Junhai(刘军海). Acta Metallurgica Sinica(金属学报). 25(4). B282(1989) |
[7] | WANG Qimin(王其闵), XIE Chenggang(谢成刚). Science in China(中国科学). A(11). 1194(1986) |
[8] | XU Yunhua(许云华). XIONG Jianlong(熊建龙), WU Hong(武宏). FU Yonghong(傅涌红), CHEN Yumei(陈渝湄). ZHU Jinhua(朱金华), Chinese Journal of Materials Research( 材料研究学报). 14(6). 665(2000) |
[9] | XU Yunhua(许云华). CHEN Yumei(陈瑜眉), XIONG Jianlong(熊建龙). ZHU Jinhua(朱金华). Acta Metallurgica Sinica(金属学报), 37(2). 165(2001) |
[10] | Zhenming HE. Qichuan JIANG, Shaobo FU and Jingpei XIE. Wear. 120. 305(1987) |
[11] | JING Tianfu, ZHANG Fucheng. Materials Letters. 31(3), 275(1997) |
[12] | ZHANG Yuhua(张玉华). ZHU Jinhua(朱金华). Journal of Xian Jiaotong University (西安交通大学学报).23(Suppl.2). 347(1989) |
[13] | A.K.Sachdev. J.E.Hunter, Jr.. Metall. Trans., 13A. 1063(1982) |
[14] | SONG Xiping(宋西平). GU Haicheng(顾海澄), Chinese Journal of Materials Research (材料研究学报),14(Suppl.1). 195(2000) |
[15] | A.M.Garde, RE.Reed-Hill, Metall. Trans., 2. 2885(1971) |
[16] | T.S.Ke Metall. Mat.Trans. A, 30A. 2267(1999) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%