研究了具有不同界面结合特性的两种复合材料在体外降解过程中吸水率、质量损失、宏现力学性能与降解时间的关系.结果表明,提高复合材料的界面结合强度可减小C/PLA复合材料的吸水率和质量损失,降低复合材料力学性能(弯曲强度、弯曲模量和剪切强度)和界面结合强度下降的速率.界面结合强度的提高对C/PLA复合材料的降解有明显的抑制作用.
参考文献
| [1] | B.Mckibbin,J.Bone Jt.Surg.,60B,150(1978) |
| [2] | P.Paavolainen,E.Karaharju,P.Slatis,J.Ahonen,T.Holmstrom,Clin.Orthop.,136,287(1978) |
| [3] | V.E.Dube,D.E.Fisher,Cancer,30,1260(1972) |
| [4] | A.Mcdougall,J.Bone Jt.Surg.,38B,709(1956) |
| [5] | S.Gogolewski,M.Jovanovic,S.M.Perren,J.G.Dillon,M.K.Hughes,J.Biomed.Mater.Res.,27,1135(1993) |
| [6] | W.Amass,A.Amass,B.Tighe,Polymer Int.,47,89(1998) |
| [7] | M.F.Gonzalez,R.A.Ruseckaite,T.R.Cuadrado,J.Appl.Polym.Sci.,71,1223(1999) |
| [8] | D.F.Williams,J.Appl.Polym.Sci.,17,1233(1982) |
| [9] | H.Elema,J.H.de Groot,A.J.Nijenhuis,A.J.Pennings,R.P.H.Veth,J.Klompmaker,H.W.B.Jansen,Colloid and Polymer Science,268,1082(1990) |
| [10] | Y.L.Wang(王玉林),Y.Z.Wan(万怡灶),Q.Y.Li(李群英),Study on in vitro degradation behavior of C/PLA composite[J](C/PLA复合材料的体外降解特性研究),Functional Materials(功能材料),32(5),553(2001) |
| [11] | A.Majola,S.Vainionpaa,P.Rokkanen,J.Mater.Sci.Mater.Med.,3,43(1992) |
| [12] | J.Kettunen,E.A.Makela,H.Miettinen,T.Nevalainen,M.Heikkila,T.Pohjonen,P.Tormala,P.Rokkanen,Biomaterials,19,1219(1998) |
| [13] | Y.Z.Wan(万怡灶),Perfomance Modulation and Swelling/Degradation Behaviors ofthe Composites for Internal Fixation Devices(骨折内固定用复合材料的性能控制及溶胀/降解行为研究),Ph.D.degree thesis(天津大学博士学位论文),Tianjin University,2000 |
| [14] | M.Ibnabddjalil,I.H.Loh,C.C.Chu,N.Blumenthal,H.Alexander,D.Turner,J.Biomed.Mater.Res.,28,289(1994) |
| [15] | M.A.Slivka,C.C.Chu,I.A.Adisaputro,J.Biomed.Mater.Res.,36,469(1997) |
| [16] | M.A.Slivka,C.C.Chu,J.Biomed.Mater.Res.,37,353(1997) |
| [17] | C.H.Shen,G.S.Springeer,J.Comp.Mater.,10,2(1976) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%