以ZrOCl2@8H2O和TiCl4为原料,用溶胶-凝胶法制备了高取向的TiO2-ZrO2复合薄膜,研究了复合薄膜的组成结构、表面形貌和摩擦学性能结果表明,该复合薄膜均匀致密、具有四方ZrO2结构;复合薄膜具有良好的减摩抗磨性能.在0.5 N低负荷下,复合薄膜与AISI 52100钢和Si3N4对磨时的摩擦系数为0.14～0.20,耐磨寿命大于5000次.TiO2-ZrO2复合薄膜可用作特殊工况条件下的减摩抗磨保护性涂层.
参考文献
| [1] | A.K.Jamting,J.M.Bell,M.V.Swain,L.S.Wielunski,R.Clissold,Thin Solid films,322,189(1998) |
| [2] | M.J.Paterson,P.J.K.Paterson,B.Ben-Nissan,J.Mater.Res.,13,388(1998) |
| [3] | S.C.Moulzolf,R.J.Lad,P.J.Blau,Thin solid films,347,220(1999) |
| [4] | W.M.Liu(刘维民),W.G.Zhang(张文光),Z.M.Zhang(张兆敏),B.Li(李斌),G.X.Mai(买光昕),Tribology(摩擦学学报),19(2),166(1999) |
| [5] | Z.Q.Zeng(曾智强),X.Y Xiao(萧小月),Z.L.Gui(桂治轮),L.T.Li(李龙土),Chinese Journal of Materials Research(材料研究学报),13(2),125(1999) |
| [6] | Z.Q.Zeng(曾智强),X.Y.Xiao(萧小月),Z.L.Gui(桂治轮),L.T.Li(李龙土),Chinese Journal of Materials Research(材料研究学报),13(1),42(1999) |
| [7] | X.R.Huang(黄肖容),Z.T.huang(黄仲涛),Journal of Inorganic Materials(无机材料学报),13(4),534(1998) |
| [8] | J.S.Lee,T.Matsubara,T.Sei,T.Tsuchiya,J.Mater.Res.,32,5249(1997) |
| [9] | Q.Y.Zhang(张勤远),J.Shen(沈军),X.L.Li(李小丽),T.H.Yang(杨天河),G.M.Wu(吴光明),B.Zhou(周斌),J.Wang(王珏),Chinese Journal of Materials Research(材料研究学报),14(1),96(2000) |
| [10] | Brenier R,Mugnier J,Mirica E,APPlied Surface Science,143,85(1999) |
| [11] | W.X.Xu,S.Zhu,X.C.Fu,Applied Surface Science,136,194(1998) |
| [12] | Y.X.Chen(陈云霞),W.M.Liu(刘维民),Tribology(摩擦学学报),21(4),274(2001) |
| [13] | Y.X.Chen,W.M.Liu,C.F.Ye,L.G.Yu,S.K.Qi,Mater.Res.Bull.,36(14),2605(2001) |
| [14] | F.Monte,W.Larsen,J.D.Mackenzie,J.Am.Ceram.Soc.,83(3),628(2000) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%