研究了Nd2Co17-xMnx(x=0,1,3,5,7,9,11)化合物的结构和磁性.Nd2Co17-xMnx化合物具有菱方相Th2Zn17型结构;在x比较小时,随着x的增加,化合物的单胞体积缓慢增大,而在x比较大时,随着x的增加,化合物的单胞体积迅速增大,这表明Nd2Co17-xMnx化合物在磁性状态下存在着正的自发体磁致伸缩;随着x的增加,化合物的居里点及4.2 K下的饱和磁化强度都快速下降,这表明在x比较小时,3d次晶格的Co-Co之间的铁磁交换作用起主导作用,而在x比较大时,3d次晶格中反铁磁交换作用起主要作用;在约234 K观察到了Nd2Co14Mn3化合物的自旋重取向现象.
The Nd2Co17-xMnx compounds have a rhomhedral Th2Zn17-type structure. Their unit-cell volumes increase slowly with increasing x, then rapidly with the further increase of x. This implies there is a positive spontaneous volume magnetostriction in the magnetic state for Nd2Co17-xMnx compounds. The Curie temperature and the saturation magnetization at 4.2 K of these compounds rapid drop with increase of x. This implied there is a crossover between the low x range, where the Co sublattice is ferromagnetic and the Co-Co ferromagnetic interaction is dominant, and the high x range where the antiferromagnetic interactions play a substantial role. The spin reorientation is observed at about 234 K in the Nd2Co14Mn3 compound.
参考文献
[1] | X.Z.Wei, S.J.Hu, D.C.Zeng, X.C.Kou, Z.Y.Liu, E.Bruck, J.C.P. Klaasse, F.R.De Boer, K.H.J.Buschow,J.Alloys Compds., 279, 301(1998) |
[2] | B.G.Shen, B.Liang, Z.H.Cheng, S.Y.Zhang, H.W.Zhang, W.S.Zhan, Chin. Phys. Lett., 15, 223(1998) |
[3] | S.Y.Zhang, B.G.Shen, B.Liang, R.W.Li, X.F.Ruan, B.Liang, H.W.Zhang, F.W.Wang, W.S.Zhan,L.G.Zhang, J.Phys.: Condens. Matter., 10, 2445(1998) |
[4] | B.Ling, B.G.Shen, F.W.Wang, S.Y.Zhang, Z.H.Cheng, T.Y.Zhao, W.S.Zhan, J.Phys.: Condens.Matter, 10,4474(1998) |
[5] | D.Zhang, D.P. Middleton, E.Bruck, F.R.de Boer, Z.D.Zhang, K.H.J.Buschow, J.Alloys., 259, 65(1997) |
[6] | C.H.De Groot, K.H.J.Buschow, F.R.. de Boer, Physica B. 229, 213(1997) |
[7] | HU Shejun, O.Tegus, WEI Xingzhao, Zhang Lei, ZENG Dechang, LIU Zhengyi, F.R.De Boer,K.H.J.Buschow, Acta Physics Sinica., 49, 355(2000) |
[8] | Yanming Hao, Yan Gao, Bowen Wang, Jingping Qu, Yangxian Li, Jifan Hu, and Jiachun Deng,Appl. Phys. Lett., 78, 3277(2001) |
[9] | Zhigang Sun, Hongwei Zhang, Jingyun wang, Baogen Shen, Appl.Phys. Lett., 775, 3850(1999) |
[10] | Hao Yangming, Yan Qiwei, Zhang Panlin, Sun Xiangdong, Wang Fangwei, Shen Baogen, Acta Physica Sinica (Overseas Edition). 6, 895(1997) |
[11] | G.P.Meisner, C.D.Fuerst, IEEE Trans. Magn., MAG-22, 744(1986) |
[12] | T.H.Jacobs, K.H.J.Buschow, G.F.Zhou, J.P. Liu, X.Li, F.R.deBoer, J.Magn. Magn. Matter., 104, 1275(1992) |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%