以在气/液界面和气/固界面上形成的硬脂酸单分子膜为基底电沉积金属银薄膜.改变电沉积条件,得到了具有不同微观结构、光亮、细致的纳米金属银薄膜.当底相硝酸银溶液的pH值低于7时,在气/液界面没有银膜形成,只在银丝的尖端生成棕黑色的粉末;提高镀液的pH值有利于银的沉积,且硬脂酸分子排列得越紧密,成膜性越好.随着槽电压的升高,银膜的沉积速度逐渐增大,其微观结构从树叶状逐渐向鹿角状变化.根据电沉积银薄膜的规律,分析了在单分子膜上电沉积银的生长机制,认为单分子膜及其界面的双电层结构是沉积银膜的必要条件.
参考文献
| [1] | CUI Dafu(崔大付),Physics(物理),25(1),54(1996) |
| [2] | J.F.Liu, K.Z.Yang, Z.H.Lu, J.Am. Chem. Soc., 119, 11061(1997) |
| [3] | X.Song, M.Miura, X.Xu, K.K.Taylor, S.A.Majumder, J.D.Hobbs, J.Cesarano, J.A.Shelnutt, Langmuir, 12,2019(1996) |
| [4] | Jangping Yang, Fiona C Meldrum, Janos H.Fendler, J.Phys. Chem., 99(15), 5500(1995) |
| [5] | H.Li, G.Mao, N.K.Y.Simon, Thin Solid Film, 358(1,2), 62(2000) |
| [6] | Moriguchi. Isamu, Nii. Hiroshi, Hamai. Kouhei, Naqaoka. Hidenori, Teraoka. Yasutake, Kaqawa. Shuich, Colloids and Surfaces: Physicochemical and Engineering, 103(3), 173(1995) |
| [7] | Jianping Yang, J.H.Fendler, J.Phys. Chem., 99(19), 5505(1995) |
| [8] | GUO Hetong(郭鹤桐),JIN Qixian(覃奇贤),Electrochemistry(电化学教程).(Tianjin,Tianjin University Press,2000)p.319 |
| [9] | J.H.Fendler,Interpreted by CHENG Huming(程虎明),GAO Yueying(高月英),Membrane Mimic Chemistry(膜模拟化学).(Beijing,Science Press,1991)p.62 |
| [10] | XIAO Yufang(肖玉方),YAO Zhongqi(姚钟麒),JIN Daosen(金道森),Chemical Journal(化学学报),53(3),214(1995) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%