提出了一种在纯铜表面得到大面积亚微米细晶组织及进行表面硬化处理的新工艺.在T2紫铜表面,利用连续摩擦压扭过程中产生的剧烈剪切塑性变形,使材料表面形成了一层厚为0.1~0.2 mm、晶粒直径200~300 nm的亚微米细晶组织,表面硬度比基材提高了1倍.压扭头行走速度和转速对变形区晶粒细化和硬化效果影响显著.理论分析结果表明,在垂直于行走方向上加热能量和变形程度基本均匀.
参考文献
[1] | V.R.Gertsman, On the structure and strength of ultrafine-grained copper produced by severe plastic deformation, Scripta metallurgica and mechanical, 30, 229(1994) |
[2] | R.Z.Valiev, Structure and mechanical properties of ultrafine-grained metals, Material Science and Engineering, A234~236, 59(1997) |
[3] | Chen Guojun(陈国钧),A review ofthe developmental program onthelimitingfunctional materialsin Japan,Material Review(材料导报),13(1),6(1999) |
[4] | Shen Hui(沈辉),A study of nanocrystalline Ni and nanocomposites Ni/SiO2 prepared by severe plastic deformation,Material Review(材料导报),13(2),55(1999) |
[5] | Z.Y.Liu, The effect of cumulative large plastic strain on the structure and properties of a Cu-Zn alloy,Materials science and Engineering, A242, 137(1998) |
[6] | M.Furukawa, Z.Horita, M.Nemoto, T.G.Langdon, Processing of metals by equal-channel angular pressing,Journal of Materials Science, 36(12), 2835(2001) |
[7] | S.Komura, Z.Horita, M.Nemoto, T.G.Langdon, Influence of stacking fault energy on microstructural development in equal-channel angular pressing, Journal of Materials Research, 14(10), 4044(1999) |
[8] | W.C.Chen, D.E.Ferguson, H.S.Ferguson, R.S.Mishra, Z.Jin, Development of ultrafine grained materials using the MAXStrain technology, Materials Science Forum (Switzerland), 357~359, 425(2001) |
[9] | N.Saito, Grain refinement of 1050 aluminum alloy by friction stir processing, Journal of Materials Science Letters, 20(20), 1913(2001) |
[10] | H.Utsunomiya, Y.Saito, H.Suzuki, T.Sakai, Development of the continuous shear deformation process, Journal of Engineering Manufacture, 215(B7), 947(2001) |
[11] | Du Suigeng(杜随更),Recrystallization of weld metal during friction welding of superalloy GH2132,Trans.of the China welding institution(焊接学报),17(4),229(1996) |
[12] | Du Suigeng(杜随更),Thefrictional mechanism and coefficient duringtheinitial stage ofthefriction welding Mechanical Science and Technology(机械科学与技术),16(4),703(1997) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%