研究了加有低轮廓添加剂的不饱和聚酯树脂在中低温固化时的形态,结果表明:温度对加入聚醋酸乙烯酯类LPA试样的固化形态影响不大,而加入聚苯乙烯类LPA对试样的固化形态则有较大的影响.在固化过程中极性较大的LPA更有利于从UPR相中分离出来,形成有利于补偿收缩的两相交互连续的相态结构,而玻璃转化温度与UPR的差别大并且低于固化温度的LPA,使得固化试样形成微孔有更多的时间和更高的效率对于加入聚醋酸乙烯酯类LPA的试样,试样的固化形态随着LPA含量的增加发生两次明显的转变.对于具有较高分子量的LPA,只需要加入较低的含量就能使试样形成相互连续的两相结构,而加入聚苯乙烯类LPA的试样,固化的形态随着LPA含量的增加没有明显的改变.
参考文献
| [1] | C.D.Rudd, A.C.Long, K.N.Kendall, C.G.E.Mangin, Liquid Moulding Technologies, Resin Transder Moulding, Structural Reaction Injection Moulding and Related Processing Techniques, (Ch.3,Woodhead Publishing House, Cambridge England, 1997) |
| [2] | V.M.Pattison, R.R.Hindersinn, W.T.Schwartz, J. Appl. Polym. Sci., 18, 2763(1974) |
| [3] | K.E.Aktins, In: Polymer Blends, D.R.Paul, S.Newman ed. (New York, Academic Press 1978) |
| [4] | K.E.Atkins, Low Profile Additives: Shrinkage Control Mechanism and Application, in: Sheet Molding Compound Materials: Science and Technology (Munich, Hanser, 1993) p. |
| [5] | E.G.Melby, J.M.Castro, Glass-reinforced Thermosetting Polyster Molding: Materials and Processing, Comprehensive Polymer Science, (Oergamon Press: Oxford, U.K., 1989) |
| [6] | M.Ruffier, G.Merle, J.P. Pascault, Polymer Engineering and Science, 33(8), 466(1993) |
| [7] | M.R.Kinkelaar, L.J.Lee, J. Appl. Polym. Sci., 45, 37(1992) |
| [8] | M.Kinkelaar, B.Wang, L.J.Lee, Polymer, 35(14), 3011(1994) |
| [9] | L.James Lee, J. Appl. Polym. Sci., 82(3), 738(2001) |
| [10] | Liu ChuanJun, A.H.J. Nijhof, M.S. Kiasat, H. Blokland, R. Marissen, Polymer Engineering and Science,39(1), 18(1999) |
| [11] | Kan Wang, Jihui Wang, Yingdan Zhu, The Effect of Low Profile Additives on Unsaturated Polyester Resins during Curing in Low Medium Temperature: Shrinkage Behavior Study, Key Engineering Materials, Volume 249, p.323～326, Proceedings of the 3rd China Cross-Strait Conference on Composite Material, Wuhan,China, May 7-12, 249, 323(2003) |
| [12] | Y.J.Huang, C.J.Chu, J.P. Dong, J. Appl. Polym. Sci., 78(3), 543(2000) |
| [13] | Y.J.Huang, S.C.Dong, J.P. Dong, J. Appl. Polym. Sci., 78(3), 558(2000) |
| [14] | W.Li, L.J.Lee, Polymer, 41(2), 685(2000) |
| [15] | W. Li, L.J.Lee, Polymer, 41(2), 697(2000) |
| [16] | Z.Zhang, Polymer, 41(10), 3861(2000) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%