研究了BaTiO3铁电陶瓷在恒载荷下的应力腐蚀,环境分别为湿空气、水、硅油和甲酰胺.结果表明,BaTiO3铁电陶瓷在湿空气、硅油、水和甲酰胺中都能发生应力腐蚀,其本质是介质分子吸附降低表面能.在空气中的瞬时断裂为穿晶断裂,滞后断裂大部分为穿晶断裂,局部为沿晶断裂.在这四种环境中,归一化应力腐蚀门槛应力强度因子分别为KIsCC/KIC=0.78(空气),0.63(水),0.66(硅油)和0.82(甲酰胺),其断裂韧性为KIC=1.29±0.14 MPa·m1/2.
参考文献
| [1] | C.P. Chen, W.J.Knapp, J Am. Ceram. Soc., 60, 87(1977) |
| [2] | J.E.Ritter, J.N.Humenik, J. Mater. Sci., 14, 626(1979) |
| [3] | S.M.Spearing, F.W.Zok, A.G.Evans, J. Am. Ceram. Soc., 77, 562(1994) |
| [4] | T.Okabe, M.Kido, T.Miyahara, Eng. Fract. Mech., 48, 137(1994) |
| [5] | E.Iskevitch, R.Chaim, Phil. May., 61, 209(1990) |
| [6] | Y.Wang, W.Y.Chu, K.W.Gao, Y.J.Su, L.J.Qiao, Appl. Phys. Lett., 82, 1583(2003) |
| [7] | Y.Wang, W.Y.Chu, Y.J.Su, L.J.Qiao, Mater. Lett., 57, 1156(2003) |
| [8] | Y.Wang, W.Y.Chu, Y.J.Su, L.J.Qiao, Mater. Sci. Eng., 95, 263(2002B) |
| [9] | W.Y.Chu, J.Yao, C.M.Hsiao, Metall. Trans., 15A, 729(1984) |
| [10] | Y.Wang, W,Y.Chu, L.J.Qiao, Y.J.Su, Mater. Sci. Eng. B, 98(1), 1(2003) |
| [11] | T.A.Michalske, S.W.Freiman, J. Am. Ceram. Soc., 66, 284(1983) |
| [12] | T.A.Michalske, B.C.Banker, J. Appl. Phys., 56, 2666(1984) |
| [13] | H.H.Yu, Z.Suo, Acta Mater., 47, 77(1999) |
| [14] | CHU Wuyang, Hydrogen Damage and Delayed Fracture (Beijing, Metallurgic Industry Press, 1988) p.270(褚武扬,氢损伤与滞后断裂(北京,冶金工业出版社,1988)p.270) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%