研究了加载频率、溶液pH值、氯离子浓度和氟化物转化膜等对挤压镁合金AM60疲劳寿命的影响,讨论了疲劳机理及AlMn相的作用.结果表明:在空气中10 Hz以下,疲劳寿命与频率有一定的关系;而在10 Hz以上,疲劳寿命与频率无关.AM60在中性溶液中疲劳寿命最短,在碱性溶液中疲劳寿命最长.氯离子能明显地降低疲劳寿命,含氟转化膜提高腐蚀疲劳寿命的作用不明显.断口分析表明,挤压镁合金AM60疲劳裂纹的形成与AlMn相粒子有关.在空气中,疲劳裂纹源为AlMn相粒子;而在溶液介质中,腐蚀疲劳裂纹萌生于AlMn相粒子周围的点蚀坑.
参考文献
[1] | S.L.Gouling, Met Eng. Quart, 12(2), 7(1970) |
[2] | ZENG Rongchang, HAN Enhou, LIU Lu, XU Yongbo, KE Wei, Chinese Journal of Materials Research,17(3), 241(2003)(曾荣昌,韩恩厚,刘路,徐永波,柯伟,材料研究学报,17(3),241(2003)) |
[3] | ZENG Rongchang, The Study on Corrosion and Corrosion Fatigue of Wrought Magnesium Alloys, Ph.D Thesis, Institute of Metals Research, The Chinese Academy of Sciences, 2003(曾荣昌,变形镁合金的腐蚀与腐蚀疲劳行为研究,博士论文,中国科学院金属研究所,2003) |
[4] | H.R.Mayer, H.Lipowsky, M.Papakyriacou, R.Rosch, A.Stich, S.Stanzl-Tschegg, Fatigue Fract Eng Mater Struct, 22, 591(1999) |
[5] | M.F.Horstemeyer, N.Yang, K.Gall, D.Mcdowell, J.Fan, P. Gullett, Fatigue Fract Eng Mater Struct, 25,1045(2002) |
[6] | M.Papakyriacou, H.Mayer, U.Fuchs, S.E.Stanzl-Tschegg, R.P. Wei, Fatigue Fract Eng Mater Struct, 25,795(2002) |
[7] | U.Fuchs, H.J.Liowsky, H.Mayer, M.Papakyriacou, A.Stich, S-Tschegg, B.Zettl, Mat.-wiss.u. Werkstofftech.,33, 15(2002) |
[8] | U.Fuchs, H.J.Liowsky, H.Mayer, M.Papakyriacou, A.Stich, S-Tschegg, B.Zettl, Mat.-wiss. u. Werkstofftech., 33, 117(2002) |
[9] | T.S.Shih, W.S.Liu, Y.J.Chen, Mater. Sci. Eng., A325, 152(2002) |
[10] | A.Eliezer, E. M.Gutman, E.Abramov, Unigovski Ya, J. Light Metals, 1, 179(2001) |
[11] | T.K.Aune, D.L.Albright, O.rjasaeter, O.K.Nerdahl, Elements of the Fatigue Process in Magnesium Die Casting Alloys, in Magnesium Technology , edited by H I Kaplan, J N Hryn, B B Clow (Warrendale, TMS.2000) p.319 |
[12] | ZHU Zufang, Corrosion Resistance and Application of Non-Ferrous Metals (Beijing, Chemistry Industry Press, 1999)p.72(朱祖芳,有色金属的耐腐蚀性及其应用,北京,化学工业出版社,1999)p.72) |
[13] | E.M.Gutman, Unigovski Ya, A.Eliezer, E.Abramov, L.Riber, Light Metal Age, 14(2000) |
[14] | M.Hilpert, L.Wagner, J. Mater. Eng. Performance, 9, 402(2000) |
[15] | T.Kanadani, A.Saijo, M.Hino K.Saki, J. Jpn. Inst. Light Metals, 52(10), 477(2002) |
[16] | ZENG Rongchang, HAN Enhou, KE Wei, Acta Metall Sinica, 44(3), (2005)(曾荣昌,韩恩厚,柯伟,金属学报,44(3),(2005)) |
[17] | ZHOU Xiangyang, KE Wei, Acta Metall Sinica, 3, 320(1990) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%