应用对靶磁控溅射法在玻璃基底上制备了类三明治结构C/Co/C纳米颗粒膜,并进行了原位退火.发现磁性层厚度对C/Co/C颗粒膜的微结构和磁特性有明显影响.在400℃退火的样品具有很好的六角密堆积结构,磁矩很好的排列在膜面内.随着磁性层Co层厚度的增加,矫顽力Hc先增大然后减小,粒径和磁畴簇略微增大,样品的表面粗糙度Ra也减小到了0.5 nm左右.
参考文献
| [1] | J.-J.Delaunay, T.Hayashi, M.Tomita, S.Hirono, S.Umemure, Appl. Phys. Lett., 71(23), 3427(1997) |
| [2] | C.P. Luo, D.J.Sellmyer, Appl. Phys. Lett., 75(20), 3162(1999) |
| [3] | Yingfan Xu, Z.S.Shan, Jian Ping Wang, Chong Tow Chong, J. Magn. Magn. Mater., 232, 103(2001) |
| [4] | I.Panagiotopoulos, S.Stavroyiannis, D.Niarchos, J.A.Christodoulides, G.C.Hadjipanayis, J. Appl. Phys.,87(9), 4358(2000) |
| [5] | Yingfan Xu , Jian Ping Wang, Ying Su, J. Appl. Phys., 87(9), 6971(2000) |
| [6] | Michael F. Toney, Ernesto E.Marinero, Mary F. Doerner, Philip M.Rice, J. Appl. Phys., 94(6), 4018(2003) |
| [7] | T.J.Konno, R.Sinclair, Acta. Metall. Mater., 42, 1231(1994) |
| [8] | T.Hayashi, S.Hirono, M.Tomita, S.Umemura, Nature(London), 381(6585), 772(1996) |
| [9] | H.Wang, S.P. Wong, W.Y.Cheung, N.Ke, J. Appl. Phys., 88(8), 4919(2000) |
| [10] | J.-J.Delaunay, T.Hayashi, M.Tomita, S.Hirono, J. Appl. Phys., 82(5), 2200(1997) |
| [11] | T.J.Konno, K.Shoji, K.Sumiyama, K.Suzuki, J. Magn. Magn. Mater., 195, 9(1999) |
| [12] | J.Shi, M.Azumi, O.Nittono, Appl. Phys., A73, 215(2001) |
| [13] | M.Yu, Y.Liu, D.J.Sellmyer, J. Appl. Phys., 85(8), 4319(1999) |
| [14] | Zuoyi Li, Long You, Zhen Li, Xiaofei Yang, Xiaomin Cheng, Fang Jin, Gengqi Lin, J. Magn. Magn. Mater.,280, 419(2004) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%