将H59双相多晶黄铜冷轧变形后,进行高密度脉冲电流处理.在透射电镜下观察发现,α+β'双相粗晶组织均已发生超细晶化转变,而且在α相晶粒中伴有大量的孪晶.经过预应变处理后,α相在脉冲电流作用下发生再结晶细化,并在随后的α→β相变中进一步发生相变细化;β'相在预应变处理后发生再结晶细化.再结晶细化的原因是,预应变处理使晶体中产生大量的缺陷,极大的增加了形核率,而脉冲电流作用时间短,加热速度快,使晶核长大不充分;相变细化的原因是,高密度脉冲电流改变了相变势垒,促进了高电导率相的形核并抑制其长大.
参考文献
| [1] | H.Conrad, N.Karam, S.Mannan, Scripta Metall., 17, 411(1983) |
| [2] | H.Conrad, N.Karam, S.Mannan, Scripta Metall., 18, 275(1984) |
| [3] | H.Conrad, N.Karam, S.Mannan, A.F.Sprecher, Scripta Metall., 22, 235(1988) |
| [4] | H.Conrad, Z.Guo, A.F.Sprecher, Scripta Metall Mater, 24, 359(1990) |
| [5] | H.Conrad, Mater Sci Eng, A287, 227(2000) |
| [6] | W. Zhang, M.L.Sui, K.Y.Hu, D.X.Li, X.N.Guo, G.H.Hc, B.L.Zhou, J. Mater. Res., 15, 2065(2000) |
| [7] | Y.Z.Zhou, W. Zhang, M.L.Sui, D.X.Li, G.H.He, J.D.Guo, J. Mater. Res., 17, 921(2002) |
| [8] | Y.Z.Zhou, W.Zhang, B.Q.Wang, J.D.Guo, J. Mater. Res., 18, 1991(2003) |
| [9] | H.Conrad, A.F.Sprecher, Dislocations in Solids (Elsevier Publisher B.V., Amsterdam, The Netherlands,1989) p.512 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%