应用取向分布函数(ODF)研究和分析了异步轧制高纯铝箔的形变织构和再结晶织构.结果表明:异步轧制高纯铝箔的形变织构除了C{112}<111>、B{110}<112>和S{123}<634>织构组分外,还有较强的CubeND{001}<110>和{102}
参考文献
[1] | A.L.Dons,E.Nes,Materials Science and Technology,2(1),8(1986) |
[2] | O.Engler,Y.H.Moo,Materials Science and Engineering,A271,371(1999) |
[3] | ZHOU Hongzhang,ZHOU Zhuoping,MENG Ya,ZHANG Xinming,The Chinese Journal of Nonferrous Metals,9(1),19(1999)(周鸿章,周卓平,孟亚,张新明,中国有色金属学报,9(1),19(1999)) |
[4] | D.N.Lee,Scripta Metallurgica et Materialia,32(10),1689(1995) |
[5] | LIU Gang,LIU Guilan,QI Kemin,WANG Fu,ZUO Liang,LIANG Zhide,Chinese Journal of Materials Research,12(4),431(1998)(刘刚,刘桂兰,齐克敏,王福,左良,梁志德,材料研究学报,12(4),431(1998)) |
[6] | LU Aiqiang,HUANG Tao,WANG Fu,ZUO Liang,The Chinese Journal of Nonferrous Metals,13(1),56(2003)(吕爱强,黄涛,王福,左良,中国有色金属学报,13(1),56(2003)) |
[7] | HUANG Tao,QU Jiahui,HU Zhuochao,WANG Fu,ZUO Liang,Acta Metallurgica Sinica,41(9),953(2005)(黄涛,曲家惠,胡卓超,王福,左良,金属学报,41(9),953(2005)) |
[8] | LIANG Zhide,XU Jiazhen,WANG Fu,Three Dimensional Orientation Distribution Analysis of Textured Materials (Shenyang,Northeastern University Press,1986) p.108(梁志德,徐家桢,王福,织构材料三维取向分析术ODF分析(沈阳,东北工学院出版社,1986)p.108) |
[9] | J.Hjelen,R.Orsund,E.Nes,Acta Metallurgica et Materialia,39(7),1377(1991) |
[10] | E.Nes,H.E.Vante,Z.Metallkde,87(6),448(1996) |
[11] | H.E.Vatne,O.Daaland,Materials Science Forum,157-162,1087(1994) |
[12] | B.J.Duggan,C.S.Lee,Scripta Metall.Mater.,27(11),1503(1992) |
[13] | F.Montheillet,M.Cohen,J.J.Jonas,Acta Metall.,32(11),2077(1984) |
[14] | F.Montheillet,P.Gilormini,J.J.Jonas,Acta Metall.,33(4),705(1985) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%