分析了CrTiAlN镀层的组织,研究了CrTiAlN镀层对M2高速钢刀具切削性能的影响.结果表明:CrTiAlN镀层提高了M2基高速钢刀具的切削性能.CrTiAlN镀层具有良好的高温稳定性能,能避免红硬性不足引起的刀具失效;CrTiAlN镀层与M2基体的结合较强,具有稳定结构,能避免抗压强度下降引起的刀具失效.
参考文献
[1] | B.Mills,Journal of Materials Processing Technology,56,16(1996) |
[2] | C.Kwietniewski,W.Fontana,C.Moraes,A.da S.Rocha,T.Hirsch,A.Reguly,Surface and Coatings Technology,179,27(2004) |
[3] | V.Derflinger,H.Brandle,H.Zimmermann,Surface and Coatings Technology,113,286(1999) |
[4] | F.Klocke,T.Krieg,Annals of the CIRP,48,515(1999) |
[5] | Andreas N.Panckow,Jorg Steffenhagen,Friedhelm Lierath,Surface and Coatings Technology,163,128(2003) |
[6] | S.G.Harris,A.C.Vlasveld,E.D.Doyle,P.J.Dolder,Surface and Coatings Technology,133~134,383(2000) |
[7] | Sture Hogmark,Staffan Jacobson,Mats Larsson,Wear,246,20(2000) |
[8] | ZHU Zuming,GUO Yanfeng,SHI Nanlin,ZHU Guiqiu,FENG Jiwei,Chinese Journal of Materials Reasearch,16(1),67(2002)(朱祖铭,郭延风,石南林,朱桂秋,冯纪伟,材料研究学报,16(1),67(2002)) |
[9] | Z.-H.Jin,Surface and Coatings Technology,179,210(2004) |
[10] | Dennis G.Teer,Magnetron Sputter Ion Plating,United Kingdom,3rd Feb.1993,GB2258343 |
[11] | Dennis G.Teer,Magnetron Sputter Ion Plating,USA,17th Sept.1996,USA5556519 |
[12] | Dennis G.Teer,Magnetron Sputter Ion Plating,Europe,7th Jan.1993,EP0521045 |
[13] | H.K(o)Tonshoff,A.Mohlfeld,Surface and Coatings Technology,93,88(1997) |
[14] | ZHAO Hongyu,FAN Qiulin,SONG Lixin,SHI Erwei,HU Xingfang,Journal of Inorganic Materials,10(1),9(2004)(赵红雨,范秋林,宋力昕,施尔畏,胡行方,无机材料学报,10(1),9(2004)) |
[15] | Allan Mathews,Surface and Coatings Technology,115,222(1999) |
[16] | H.Schulz,E.Bergmann,Surface and Coatings Technology,50,53(1991) |
[17] | X.T.Zeng,S.Zhang,C.Q.Sun,Thin Solid Films,424,99(2003) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%