以热力学和动力学理论为基础,研究了Nb微合金钢热变形过程中铁素体相的形核及长大过程,在形核速率计算中引入变形储能、晶界凸阶及微合金元素的作用,建立了低温变形诱导铁素体相变的动力学模型,分析了热变形参数和化学成分对相变分数和晶粒尺寸的影响.变形温度的降低和变形程度的增加,促进了α相变过程,相变体积分数增加,晶粒得到细化.C与Mn含量增加的效果则相反.模型应用于热轧带钢生产过程的模拟,计算结果和实测结果吻合良好.
参考文献
| [1] | R.Priestner,Metallurgical Society of AIME,455,(1981) |
| [2] | R.Priestner,L.Ali,Mater.Sci.Tech.,9,135(1993) |
| [3] | Y.Mstsumura,H.Yada,Trans.ISIJ,27,492(1987) |
| [4] | J.H.Beynon,R.Gloss,P.D.Hodgson,Mater.Forum,16,37(1992) |
| [5] | M.R.Hickson,P.J.Hurley,R.K.Gibbs,G.L.Kelly,P.D.Hodgson,Metall.Trans.A.,33A,1019(2002) |
| [6] | WANG Guodong,LIU Xianghua,LI Weijuan,DU Linxiu,ZHANG Hongmei,YUAN Jianguang,ZHANG Pijun,Iron and steel,36(5),39(2001)(王国栋,刘相华,李维娟,杜林秀,张红梅,袁建光,张丕军,钢铁,36(5),39(2001)) |
| [7] | M.Umemmto,Acta Metall.,34,1377(1986) |
| [8] | K.S.Cahn,J.K.Lee,G.J.Shiflet,H.I.Aaronson,Metall.Trans.,9A,1016(1978) |
| [9] | J.W.Cahn,Acta Metall,4,449(1956) |
| [10] | M.Umemoto,A.Hiramatsu,A.Moriya,T.Watanabe,S.Nanba,N.Nakajima,G.Anan,Y.Higo,ISIJ International,32,306(1992) |
| [11] | F.Siciliana Jr.,K.Minamai,T.M.Maccagno and J.J.Jonas.ISIJ Int.,36,1500(1996) |
| [12] | M.Umemoto,H.Ohtsuka,I.Tamura,THERMEC-88,Tokyo,2,769(1988) |
| [13] | K.J.Lee,J.K.Lee,K.B.Kang,O.Kwon.,ISIJ International,32,326(1992) |
| [14] | B.Dutta,E.J.Palmiere,C.M.Sellars,Acta Mater.,49,785(2001) |
| [15] | M.Hillert,Metall.Trans.,6A,5(1975) |
| [16] | DONG Han,XUN Xinjun,LIU Qingyou,WENG Yuqing,Iron and Steel,38(10),56(2003)(董瀚,孙新军,刘清友,翁宇庆,钢铁,38(10),56(2003)) |
| [17] | HU Yanhui,DU Linxiu,GAO Cairu,LIU Xianghua,LI Hongbin,HAN Wei,Iron and Steel,39(10),54(2004)(胡燕慧,杜林秀,高彩茹,刘相华,李宏斌,韩伟,钢铁,39(10),54(2004)) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%