将含碳量(质量分数)为0.057%和0.18%的低碳钢在不同过冷度、变形温度、变形速率和变形量的条件下进行热模拟实验,研究了含碳量和热变形条件对超细晶粒形成的影响.结果表明,变形前快速冷却(20℃/s)至Ar3以上附近温度并进行超过50%变形量的变形,能强烈促进过冷奥氏体形变诱发铁素体相变,铁素体在奥氏体晶内平行的变形带上形核,并发生动态回复和再结晶,从而使组织细化.形变诱发的相变过程由碳的扩散所控制,当钢的含碳量比较高时,小过冷度、大变形量和中等变形速率有利于铁素体相变,晶界碳化物的析出能够抑制铁素体晶粒的长大,因而高碳含量钢表现出更好的细化晶粒效果.
参考文献
| [1] | R.Priestner,P.D.Hodgson,Mater.Sci.Technol.,8(10),849(1992) |
| [2] | Yoshikasu Matumura,Hiroshi Yada,Trans.ISIJ,27,492(1987) |
| [3] | Yoshitaka Adachi,Toshiro Tomida,Shigeharu Hinotani,Iron and Steels,85,50(1999) |
| [4] | S.Torizuka,O.Umezawa,K.Tsuzaki,K.Nagai.CAMP-ISIJ,11,565(1998) |
| [5] | R.K.Brzuszek,P.C.M.Rodrigues,L.S.Motta,Materials Research,5,3(2002) |
| [6] | B.Sarkar,B.K.Jha,V.Kumar,J.of Materials Engineering and Performance,14,2(2005) |
| [7] | R.Z.Wang,Z.M.Yang,Y.Zhao,Research of Iron and Steels,4,21(2001)(王瑞珍,杨忠民,赵燕,钢铁研究,4,21(2001)) |
| [8] | H.M.Zhang,X.H.Liu,G.D.Wang,J.Northeastern University,22,431(2001)(张红梅,刘相华,王国栋,东北大学学报,22,431(2001)) |
| [9] | W.Y.Yang,A.M.Hu,J.J.Qi,Chinese Journal of Materials Research,15,171(2001)(杨王玥,胡安民,齐俊杰,材料研究学报,15,171(2001)) |
| [10] | M.R.Hickson,P.J.Hurley,R.K.Gibbs,G.L.Kelly,and P.D.Hodgson,Metallurgical and Materials Transanctions A,33A(4),1019(2002) |
| [11] | R.Priestner,L.Ali,Mater.Sci.Technol.,9,26(1993) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%