研究了约束态加热过程中产生的回复力对TiNi形状记忆合金剩余马氏体的影响.结果表明,产生的回复力使剩余马氏体发生了塑性变形,使逆相变温度升高,剩余马氏体分数和其逆相变温度之间存在特定的函数关系.但是,外部约束条件的变化对马氏体的自拉伸过程所造成的剩余马氏体分数与其逆相变温度之间的关系影响很小.
参考文献
| [1] | Z.G.Wei,R.Sandstrom,S.Miyazaki,J.Mater.Sci.,33,3743(1998) |
| [2] | Z.G.Wei,R.Sandstrom,J.Mater.Sci.,33,3763(1998) |
| [3] | S.Furuya,A.Sasaki,M.Taya,Mater.Trans.JIM,34,224(1993) |
| [4] | LI Yan,CUI Lishan,ZHENG Yanjun,YANG Dazhi,Chinese Journal of Materials Research,15(6),649(2001)(李岩,崔立山,郑雁军,杨大智,材料研究学报,15(6),649(2001)) |
| [5] | Y.Li,L.Cui,X.Zhao,D.Yang,Mater.Sci.Forum,394～395,265(2002) |
| [6] | L.Cui,Y.Li,Y.Zheng,D.Yang,Mater.Lett.,47,286(2001) |
| [7] | LIU Xiaopeng,JIN Wei,MENG Changgong,CHAO Mingzhou,YANG Dazhi,Acta Metall.Sin.,37(6),589(2001)(刘晓鹏,金伟,孟长功,曹名洲,杨大智,金属学报,37(6),589(2001)) |
| [8] | LIU Xiaopeng,JIN Wei,CHAO Mingzhou,YANG Rui,Acta Metall.Sin.,40(2),130(2004)(刘晓鹏,金伟,曹名洲,杨锐,金属学报,40(2),130(2004)) |
| [9] | Y.Zheng,J.Schrooten,L.Cui,J.Van Humbeeck,Acta Materialia,51,5467(2003) |
| [10] | Y.Zheng,L.Cui,Y.Li,D.Yang,J.Mater.Sci.Technol.,20(4),390(2004) |
| [11] | Y.Zheng,L.Cui,J.Schrooten,Appl.Phys.Lett.,84,31(2004) |
| [12] | Z.G.Wang,X.T.Zu,S.Zhu,L.M.Wang,Mater.Lett.,59,491(2005) |
| [13] | Y.Zheng,L.Cui,F.Zhang,D.Yang,J.Mater.Sci.Technol.,16,611(2000) |
| [14] | M.Piao,K.Otsuka,S.Miyazaki,Mater.Trans.JIM,34,919(1993) |
| [15] | H.C.Lin,S.K.Wu,T.S.Chou,H.P.Kao,Metall.Mater.,39,2069(1991) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%