提出了一种用微弯曲实验测定材料的与应变梯度塑性相联系的内禀长度的新方法.由一组不同的加载时曲率半径Ri和对应的卸载后曲率半径RFi的比值与Ri的关系,求出屈服强度与杨氏模量的比和硬化系数与杨氏模量的比;再应用这两个比值求出不同样品厚度的无量纲弯曲力矩与表面应变的实验关系曲线,对曲线拟合求出材料的内禀长度.将这种方法用于测定铝的内禀材料长度,研究其弯曲强度的尺寸效应,所得结果与前人用微弯曲和微拉伸两种实验方法得到的结果符合得很好.
参考文献
| [1] | N.A.Fleck,G.M.Muller,M.F.Ashby,J.W.Hutchinson,Strain gradient plasticity:theory and experiment,Acta Metal.Mater.,42,475(1994) |
| [2] | N.A.Fleck,J.W.Hutchinson,Strain gradient plasticity,Advances in Applied Mechanics,33,295(1997) |
| [3] | H.Gao,Y.Huang,W.D.Nix,J.W.Hutchinson,Mechanism-based strain gradient plasticity.Ⅰ.Theory,J.Mech.Phys.Solids,47,1239(1999) |
| [4] | Y.Huang.,H.Gao,W.D.Nix,J.W.Hutchinson,Mechanism-based strain gradient plasticity-Ⅱ.Analysis,J.Mech.Phys.Solids,48,99(2000) |
| [5] | J.S.St(o)lken,A.G.Evans,A microbend test method for measuring the plasticity length scale,Acta Materialia,46,5109(1998) |
| [6] | P.Shrotriya,S.M.Allameh,J.Lou,T.Buchheit,W.O.Soboyejo.On the measurement of the plasticity length scale parameter in LIGA nickel foils,Mechanics of Materials,35,233(2003) |
| [7] | M.A.Haque.M.T.A.Sail,Strain gradient effect in nanoscale thin films,Acta Materialia,51,3053(2003) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%