采用熔融玻璃净化配合循环过热使Ni-32.5%Sn(质量分数)共晶合金实现了深过冷快速凝固.当过冷度大于某一临界值时,非规则共晶在凝固组织中出现.随着过冷度的提高,最终得到完全的非规则共晶组织.通过分析Ni-Sn共晶合金中各相形核、生长、以及枝晶熔断机制随过冷度的变化,解释了非规则共晶的形成机制.在深过冷条件下熔体中初生相率先形核并长入过冷熔体中,形成枝晶骨架,再辉重熔后次生相从残余熔体中析出并包围初生相,形成非规则共晶.
参考文献
| [1] | T.Z.Kattamis,M.C.Flemings,Structure of undercooled Ni-Sn eutectic,Metall.Trans.,1,1449(1970) |
| [2] | B.L.Jones,Growth mechanisms in undercooled eutectics,Metall.Trans.,2,2950 (1971) |
| [3] | B.Wei,D.M.Herlach,B.Feuerbacher,F.Sommer,Dendritic and eutectic solidification of undercooled Co-Sb alloys,Acta Metal.,41,1801(1993) |
| [4] | L.Q.Xing,D.Q.Zhao,X.C.Chen,Solidification of undercooled Ni-32.5%Sn eutectic alloy,J.Mater.Sci.,28,2733(1993) |
| [5] | D.Chen,G.C.Yang,F.Liu,C.L.Yang,Y.Z.Chen,Y.P.Lu,N.Liu,Y.H.Zhou,Structural evolution and anomalous eutectic formation of highly undercooled Ni-Sn alloys,Progress in Natural Science,16(2),248(2006)(陈达,杨根仓,刘峰,杨长林,陈豫增,卢一平,刘宁,周尧和,深过冷Ni-Sn共晶合金凝固组织的演化及非规则共晶的形成,自然科学进展,16(2),248(2006)) |
| [6] | D.M.Herlach,F.Gillessen,T.Volkmann,M.Wollgarten,K.Urban,Phase selection in undercooled quaicrtstalforming Al-Mn alloy melts,Phys.Rev.B,46,5203(1992) |
| [7] | G.Shao,P.Tsakiropoulos,Prediction of phase selection in rapid solidification using time dependent nucleation theory,Acta Metall.Mater.,42,2937(1994) |
| [8] | Y.P.Lu,G.C.Yang,C.L.Yang,H.P.Wang,Y.H.Zhou,Phase-selection and metastable phase formation in highly undercooled eutectic Ni78.6Si21.4 alloys,Progress in Natural Science,to be pressed(卢一平,杨根仓,杨长林,王海鹏,周尧和,深过冷Ni78.6Si21.4共晶合金相选择与亚稳相的形成,自然科学进展,待发表) |
| [9] | Liu Y.C.,Phase selection and controlling in rapidly solidified Ti-Al alloys,Ph.D.thesis,Northwestern Polytechnical University,2000)(刘永长,快速凝固Ti-Al包晶合金的相选择与控制,博士学位论文,西北工业大学(2000)) |
| [10] | Yang C.L.,Yang G.C.,Liu F.,Chen Y.Z.,Liu N.,Chen D.,Zhou Y H,Metastable phase formation in eutectic solidification of highly undercooled Fe83B17 alloy melt,Phys B,373,136 (2006)(杨长林,杨根仓,刘峰,陈豫增,刘宁,陈达,周尧和,深过冷Fe83B17共晶合金熔体的亚稳相的形成,Phys.B,373,136(2006) |
| [11] | Lipton J.,Kurz W.,Trivedi R.,Rapid dendrite growth in undercooled melts,Acta Metal,35,957(1987) |
| [12] | Boetinger W.J.,Coriell S.R.,Trivedi R.,in:Mehrabian R.(eds),Proceedings of the Fourth Conference on Rapid Solidification Processing,Principles and Technologies,Claitors,Baton Rouge,LA,1987:p.13 |
| [13] | Trivedi R.,Magnin P.,Kurz W.,Theory of eutectic growth under rapid solidification conditions,Acta Metall.,35,971(1987) |
| [14] | Li J.F.,Liu Y.C.,Lu Y.L.,Yang G.C.,Structural evolution of undercooled Ni-Cu alloys,J.Crystal Growth,192,528(1998) |
| [15] | Hu Z.Z.,High undercooling and basic solidification regulations of bulk Ni-based eutectic alloys,Ph.D.thesis,Northwestern Polytechnical University,1998)(惠增哲,大体积Ni基共晶系合金的深过冷与凝固规律,博士学位论文,西北工业大学(1998)) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%