用交流电位降(ACPD)技术实现了模拟压水堆一回路340℃高温水环境中690合金应力腐蚀裂纹扩展的实时监测.断口观察表明,2种一维冷加工690合金均出现沿晶应力腐蚀裂纹扩展,裂纹沿平行轧制方向的扩展速率略高于垂直轧制方向的速率;当溶解H浓度(CdH)由30 μL/g减小到10 μL/g时,经1075℃退火和700℃固溶处理15h并--维冷轧25%的T-L取向690合金的平均裂纹扩展速率由4.8×10(-11)m/s增加至11.2×10(-11)m/s;应力腐蚀裂纹扩展主要为内氧化机制.
参考文献
[1] | Speidel M O,Magdowski R.In:Gold R E,Simonen E P,eds.,6th Int Symp Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors,California= TMS,1993:361 |
[2] | Moshier W C,Brown C M.Corrosion,2000;56:307 |
[3] | Yamazaki S,Lu Z P,Ito Y,Takeda Y,Shoji T.Corro Sci,2008;50:835 |
[4] | Rebak R B,Szklarska-Smialowska Z.Corro Sci,1996;38:971 |
[5] | Page R A,Mcminn A.Metall Tram,1986;17A:877 |
[6] | Alexandreanu B,Chopra O,Shack W.13th Int symp Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors.British Columbia:CNS,Aug 19-23,2007 |
[7] | Andresen P L,Morra M M,Hickling J,Ahluwalia K S,Wilson J A.18th Int Symp Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors.British Columbia:CNS,Aug 13-23,2007 |
[8] | Olszta M,Edwards D,Bruemmer S.ICG-EAC 2008 Conference.Bastad Sweden,Apr 20-25,2008 |
[9] | Andresen P L,Hickling J,Ahluwalia A,Wilson J.ICGEAC 2008 Conference.Bastad Sweden,Apr 20-25,2008 |
[10] | Andresen P L,Hickling J,Ahluwalia A,Wilson J.Corrosion,2008;64:707 |
[11] | Vaillant F,Mitheux J D,Bouvier O,Vancon D,Zacharie G,Brechet Y,Louchet F.In:Ford F P,Bruemmer S M,Was G S,eds.,9th Int Symp Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors,Pennsylvania:TMS,1999:251 |
[12] | Sui G,Titchmarsh J M,Heys G B,Congleton J.Corros Sci,1997;39:565 |
[13] | [13) Scenini F,Newman R C,Cottis R A,Jacko R J.In:Allen T R,King P J,Nelson L,eds.,12th Int Symp Environmen-tal Degradation of Materials in Nuclear Power Systems Water Reactors,Pennsylvania:TMS,2005:891 |
[14] | Young B A,Gao X,Srivatsan T S,King P J.Mater Des,2007;28:373 |
[15] | Lu Z,Shoji T,Takeda Y,Kai A,Ito Y.Corrosion,2007;63:1020 |
[16] | Lu Z P,Shoji T,Takeda Y,Ito Y,Yamazaki S.Corros Sci,2008;50:698 |
[17] | Lu Z P,Shoji T,Takeda Y,Ito Y,Kai A,Tsuchiya N.Corros Sci,2008;50:625 |
[18] | Lu Z P,Shoji T,Takeda Y,Ito Y,Kai A,Yamazaki S.Corros Sci,2008;50:561 |
[19] | Zhang H B,Li S J,Hu Y H,Xie X S,Wang J Z.Spec Steel Technol,2003;8(4):2(张红斌,李守军,胡尧和,谢锡善,王剑志.特钢技术,2003;8(4):2) |
[20] | Dan T C.PhD Thesis,Institute of Metal Research,Chinese Academy of Sciences,Shenyang,2010(但体纯.中国科学院金属研究所博士学位论文,沈阳,2010) |
[21] | Shen Y,Shewmon P G.Metall Trans,1991;22A:1857 |
[22] | Arioka K,Yamada T,Terachi T,Miyamoto T.Corrosion,2008;64:691 |
[23] | Lu Z,Shoji T,Dan T,Qiu Y,Yonezawa T.Corros Sci,2010;52:2547 |
[24] | Shoji T,Lu Z P,Das N K,Murakami H,Takeda Y,Ismail T.2009 ASME Pressure Vessels and Piping Conference,New York:ASME,2009:1 |
[25] | Marchetti L,Perrin S,Raquet O,Pijolat M.Mater Sci Forum,2008;595-598:529 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%