通过水溶液镀Cr后再用AlCl3-EMIC(氯化1-甲基3-乙基咪唑)离子液体镀Al,制备Cr/Al复合镀层,其后通过低温扩散热处理制备Al-Cr涂层.用OM,SEM,BSE,EDS和XRD研究了短时间热处理时,热处理温度对Al-Cr涂层组成和结构的影响.结果表明,Cr/Al复合镀层在540℃时即可发生明显的互扩散,形成Al-Cr合金层.通过对复合镀层中Cr和Al镀层厚度的控制,可以得到不同组成的Al-Cr合金涂层.6.5 μm Cr/15 μm Al的复合镀层经640℃/960 min热处理,表面形成以Al8Cr5为主的合金涂层;1.6 μm Cr/15 μm Al的复合镀层经600℃/30 min热处理,可得到以Al4Cr为主的Al-Cr涂层.
参考文献
| [1] | Zhang Y,Pint B A,Cooley K M,Haynes J A.Surf Coat Technol,2008; 202:3839 |
| [2] | Konys J,Aiello A,Benamati G,Giancarli L.Fus Sci Technol,2005; 47:844 |
| [3] | Han S L,Li H L,Wang S M,Jiang L J,Liu X P.Int J Hydrogen Energy,2010; 35:2689 |
| [4] | Geib F D,Rapp R A.Oxid Met,1993; 40:213 |
| [5] | Xiang Z D,Datta P K.Surf Coat Technol,2004; 184:108 |
| [6] | Wang Y Q,Zhang Y,Wilson D A.Surf Coat Technol,2010; 204:2737 |
| [7] | Si X,Lu B,Wang Z.J Mater Sci Technol,2009; 25:433 |
| [8] | Xiang Z D,Rose S R,Datta P K,Scheeffer M.Surf Coat Technol,2009; 203:1225 |
| [9] | Li Y,Ling G P,Liu K Z,Chen C A,Zhang G K.Trans Mater Heat Treat,2009; 30(5):182(李岩,凌国平,刘柯钊,陈长安,张桂凯.材料热处理学报,2009;30(5):182) |
| [10] | Nagasaki S,Hirabayashi M.Binary Alloy Phase Diagrams,Tokyo:AGNE Gijutsu Center Co.Ltd.,2002:29 |
| [11] | He Z B,Zou B S,Kuo K H.J Alloys Compd,2006; 417:L4 |
| [12] | Cao B B,Kuo K H.J Alloys Compd,2008; 458:238 |
| [13] | Wen K Y,Chen Y L,Kuo K H.Metall Trans,1992; 23A:2437 |
| [14] | Brushko B,Przeiórzy(n)ski B,Kowalska-Strzeciwilk E,Surowiec M.J Alloys Compd,2006; 420:L1 |
| [15] | Barbier F,Manuelli D,Bouché K.Acta Metall,1997; 36:425 |
| [16] | Tunca N,Delamore G W,Smith R W.Metall Trans,1990; 21 A:2919 |
| [17] | Mahdouk K,Gachon J C.J Phase Equilibria,2000; 21(2):157 |
| [18] | Okamoto H.J Phase Equilibria Diffus,2008; 29(1):112 |
| [19] | Grushko B,Kowalska-Strzeciwilk E,Przepiórzy(n)ski B,Surowiec M.J Alloys Compd,2005; 402:98 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%