利用OM,SEM,TEM,EDS和SAEDP等方法对4种不同Ti含量的低碳Ti-Mo全铁素体基体微合金钢中析出相的尺寸、形貌,分布特征和类型进行了研究.结果表明,钢中存在2种尺寸差异明显的析出相:一种为纳米尺度粒子,是Ti和Mo的复合碳氮化物,尺寸小于10 nm,呈球形,主要为晶内析出,呈链状或弥散分布,位错节点和位错网是纳米尺度析出相的优先形核位置:另一种为大颗粒析出相,是Ti的碳氮化物,数量很少,尺寸为200-300 nm,星方形,带有"帽口".常温和高温拉伸实验表明,全铁素体纳米尺度析出钢具有良好的力学性能,其中No.4钢在600℃屈服强度仍然维持在约300 MPa,具有良好的高温性能.
参考文献
| [1] | Cao J C.PhD Thesis,Kunming University of Science and Technology,2006(曹建春.昆明理工大学博士学位论文,2006) |
| [2] | Gladman T.Mater Sci Technol,1999; 15:30 |
| [3] | Yong Q L.Secondary Phase in Steel.Beijing:Metallurgical Industry Press,2006:15(雍岐龙.钢铁材料中的第二相.北京:冶金工业出版社,2006:15) |
| [4] | Andrade H L,Akben M G,Jonas J J.Metall Trans,1983; 14A:1967 |
| [5] | Lee W B,Hong S G,Park C G,et al.Metall Mater Trans,2002; 33A:1689 |
| [6] | Lee W B,Hong S G,Park C G.Scr Mater,2000; 43:319 |
| [7] | Yang S W,He X L,Chen M D.Mater Sci Technol,1994; 12(2):49(杨善武,贺信莱,陈梦滴.材料科学与工程,1994;12(2):49) |
| [8] | Wang Z D,Qu J B,Liu X H.Acta Metall Sin,2000; 36:618(王昭东,曲锦波,刘相华.金属学报,2000;36:618) |
| [9] | He X L,Shang C J,Yang S W.High Performance Low Carbon Bainite Steel/Ingredients,Process,Microstructure,Properties and Application.Beijing:Metallurgical Industry Press,2008:152(贺信来,尚成嘉,杨善武.高性能低碳贝氏体钢-成分、工艺、组织、性能与应用.北京,冶金工业出版社,2008:152) |
| [10] | Craven A J,He K,Garvie L A J,Baker T N.Acta Mater,2000; 48:3857 |
| [11] | Hong S G,Kang K B,Park C G.Scr Mater,2002; 46:163 |
| [12] | Villars P,Calvert L D.Metals Park(USA OH):ASM,1985:52 |
| [13] | Yu W.PhD Thesis,University of Science and Technology Beijing,2008(余伟.北京科技大学博士学位论文,2008) |
| [14] | DeArdo A J.Mater Sci Forum,1998; 284-286:15 |
| [15] | Funakawa Y,Shiozaki T,Tomita K.ISIJ Int,2004; 44,1945 |
| [16] | Cao J C,Yong Q L,Liu Q Y.Trans Mater Heat Treat,2006; 27(5):51(曹建春,雍岐龙,刘清友.材料热处理学报,2006;27(5):51) |
| [17] | Bacroix B,Akben M G,Jonas J J.Warrendale:A Publication of the Metallurgy Society of AIME,1982:293 |
| [18] | Lee W B,Hong S G,Park C G,Kim K H,Park S H.Scr Mater,2000; 43:319 |
| [19] | Akben M G,Baeroix B,Jonas J J.Acta Metall,1983; 31:161 |
| [20] | Maruyama N,Uemori R,Suriyama M.Mater Sci Eng,1998; A250:2 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%