研究了在pH值分别为8,9和10的除氧硼酸缓冲溶液中,低碳钢腐蚀产物对其活化/钝化敏感性的影响.实验结果表明,在pH值为8时,低碳钢一直处于活性溶解状态,不受腐蚀产物影响;在pH值为9和10时,表面腐蚀产物使低碳钢钝化,其腐蚀电位最后稳定于钝化区间.XPS和XRD等分析结果表明,腐蚀产物由FeB(OH)12B4O7和γ-FeOOH组成.腐蚀产物覆盖的低碳钢比裸低碳钢更容易发生钝化.
参考文献
| [1] | Wersin P,Spahiu K,Bruno J.SKB Technical Report (94-02),Stockholm:Swedish Nuclear Fule and Waste Management Co.,1994 |
| [2] | Wang G,Chen J M.J Chin Soc Corros Prot,1985; 5:258(王戈,陈俊明.中国腐蚀与防护学报,1985;5:258) |
| [3] | Zhang Q C,Wu J S.Mater Rev,2000; 14:12(张全成,吴建生.材料导报,2000;14:12) |
| [4] | Almeida E,Morcillo M,Rosales B M,Marrocos M.Mater Corros,2000; 51:859 |
| [5] | Bonin P M L,Jedral W,Odziemkowski M S,Gillham R W.Corros Sci,2000; 42:1921 |
| [6] | Ateya B G,Al Kharafi F M,Abdalla R M.Mater Chem Phys,2002; 78:534 |
| [7] | Ahn S J,Kwon H S.Electrochim Acta,2004; 49:3347 |
| [8] | Hamadou L,Kadri A,Benbrahim N.Appl Surf Sci,2005; 252:1510 |
| [9] | Harrington S P,Wang F.Electrochim Acta,2010; 55:4092 |
| [10] | Nagayama M,Cohen M.J Electrochem Soc,1962; 109:781 |
| [11] | Markovac V,Cohen M.J Electrochem Soc,1967; 114:678 |
| [12] | Tokunaga K.Jpn J Appl Phys,1982; 21:1700 |
| [13] | Brion D.Appl Surf Sci,1980; 5:133 |
| [14] | Moulder J F,Stickle W F,Sobol P E,Bomben K D.Handbook of X-ray Photoelectron Spectroscopy.Waltham:Perkin-Elmer Corporation,1979:36 |
| [15] | Schreifels J A,Maybury P C,Swartz W E.J Catal,1980; 65:195 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%