采用SCN-5H2O(摩尔分数,%)透明模型合金研究了较低剪切速率范围内过冷合金熔体中晶体的生长与演化行为.结果表明,在较大过冷度下,存在一个剪切速率阈值,当熔体剪切速率高于阈值,晶体能够以球状形态生长;当剪切速率低于阈值,晶体以枝晶形态生长.在较低剪切速率下,过冷度较大时,球晶失稳后呈枝晶形态,过冷度较小时,球晶失稳后呈玫瑰晶形态.球晶失稳形成玫瑰晶是由球晶界面扰动胞低速生长过程中尖端发生持续分叉所造成的.
参考文献
[1] | Spencer D B,Mehrabian R,Flemings M C.Metall Trans,1972; 3A:1925 |
[2] | Flemings M C.Metall Trans,1991; 22B:957 |
[3] | Vogel R A,Cantor B.J Cryst Growth,1977; 37:309 |
[4] | Vogel A,Doherty R D,Cantor B.Proc Conf on Solidification and Casting of Metals,Sheffield,1977,London:Metal Society,1977:518 |
[5] | Vogel A.Met Sci,1978; 12:576 |
[6] | Molenaar J M M,Salemans F W H C,Katgerman L.J Mater Sci,1985; 20:4335 |
[7] | Doherty R D.Met Sci,1982; 16:1 |
[8] | Mullis A M.Acta Mater,1999; 47:1783 |
[9] | Ji S,Fan Z.Metall Mater Trans,2002; 33A:3511 |
[10] | Li T,Huang W D,Lin X.Chin J Nonferrous Met,2000;10:635(李涛,黄卫东,林鑫.中国有色金属学报,2000;10:635) |
[11] | Lin X,Li T,Huang W D.Solid State Phenom,2006; 16-17:155 |
[12] | Li T,Lin X,Huang W D.Acta Mater,2006; 54:481 |
[13] | Ji S,Fan Z,Bevis M J.Mater Sci Eng,2001; A299:210 |
[14] | Martinez R A,Flemings M C.Metall Mater Trans,2005;36A:2205 |
[15] | Li T.PhD Thesis,Northwestern Polytechnical Universty,Xi'an,2003(李涛.西北工业大学博士学位论文.西安,2003) |
[16] | Bian X F,Wang W M,Li H,Ma J J.The Melt Structure of Metal.Shanghai:ShangHai Jiao Tong University Press,2003:39(边秀房,王伟民,李辉,马家骥.金属熔体结构.上海:上海交通大学出版社,2003:39) |
[17] | Min N B.The Physical Fundamental of Crystal Growth.Shanghai:Shanghai Science and Technology Press,1981:226(闵乃本.晶体生长的物理基础.上海:上海科学技术出版社,1981:226) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%