研究了45CrNiMoVA铁磁钢中心裂纹试样加载条件下疲劳裂纹扩展过程中表面自发射磁信号的变化规律.结果表明:承受疲劳载荷前,各检测线呈现初始磁异变峰特征,切口中心检测线具有最大异变峰-峰值;加载后但疲劳裂纹萌生前,切口位覽磁性反转,显示一次异变峰特征,远离切口检测位置磁信号呈现线性;疲劳裂纹扩展过程中,各检测线依次呈现二次异变峰;二次异变峰-峰值和正负峰间斜率可以动态表征疲劳裂纹扩展寿命.基于磁荷概念和等效磁场理论分析了加载条件下疲劳裂纹扩展自发射磁信号行为.
参考文献
| [1] | Xu B S,Liu S C.Rernanufacture and Recycling Economy.Beijing:Science Press,2007:136(徐滨士,刘世参.再制造与循环经济.北京:科学出版社,2007:136) |
| [2] | Xu B S.Theory and Technology on Remanufacturing Engineering.Beijing:National Defence Industry Press,2007:124(徐滨士.装备再制造工程的理论与技术.北京:国防工业出版社,2007:124) |
| [3] | Doubov A A.Weld World,1998;41:196 |
| [4] | Doubov A A.Therm Eng,2001;48:289 |
| [5] | Doubov A A.Weld World,2002;46:317 |
| [6] | Li L M,Huang S L,Wang X F,Li S S,Shi K R.Trans Nonferrous Met Soc,2003;13:6 |
| [7] | Dong L H,Xu B S,Dong S Y,Chun Q Y,Wang D.NDT&E Int,2008;41:184 |
| [8] | Dong L H,Xu B S,Dong S Y,Qu M X,Wang D.Surf Eng China,2010;23:106(董丽虹,徐滨士,董世运,曲美霞,王丹.中国表面工程,2010;23:106) |
| [9] | Dong L H,Xu B S,Dong S Y,Chen Q z,Wang D.Int J Fatigue,2008;30:1599 |
| [10] | Lu L,Jiles D C.IEEE Trans Magn,2003;39:3037 |
| [11] | Lo C C H,Lee S J,Li L,Kerdus L C,Jiles D C,IEEE Trans Magn,2002;38:2418 |
| [12] | Chen Y,Jiles D C.IEEE,Trans Magn,2000;36:3244 |
| [13] | Yu F Y,Zhang C X,Wu M.Mech Des Manuf,2006;(5):118(于风云,张川绪,吴淼.机械设计与制造,2006;(5):118) |
| [14] | Dong L H,Xu B S,Dong S Y,Chen Q Z.NDT&E Int,2009;42:323 |
| [15] | Dong L H.PhD Thesis,Academy of Armored Forces Engineering,Beijing,2008 (董丽虹.装甲兵工程学院博士学位论文,北京,2008) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%