受控脉冲穿孔等离子弧焊接(PAW)过程中,小孔形状随焊接电流动态变化,经历“形成-长大-缩小-闭合”的变化过程.本文在对受控脉冲PAW瞬态温度场进行数值模拟的基础上,通过分析焊接熔池表面的受力状态,建立了小孔形状的模型,考虑了盲孔(小孔深度小于工件厚度)和穿透小孔2类情况.对焊接熔池内三维小孔在一个脉冲周期内的变化过程进行了数值计算.进行了受控脉冲PAW工艺实验,验证了穿孔持续时间的数值分析结果.
参考文献
| [1] | Wu C S,Jia C B,Chen M A.Weld J,2010; 89:225s |
| [2] | Jia C B,Wu C S,Gao J Q.Acta Metall Sin,2010; 46:991(贾传宝,武传松,高进强.金属学报,2010; 46:991) |
| [3] | Saedi H R,Unkel W.Weld J,1988; 67:247s |
| [4] | Vishnu P R,Easterling K E.Mater Sci Technol,1991; 7:649 |
| [5] | Wu C S,Zheng W,Wu L.Acta Metall Sin,1998; 34:416(武传松,郑炜,吴林.金属学报,1998; 34:416) |
| [6] | Reddy A A,Guta B,Achar D R G.Numer Heat Trans,2002; 41A:41 |
| [7] | Liu W L,Hu S S,Ma L.Trans China Weld Inst,2006;26(6):33(刘望兰,胡绳荪,马立.焊接学报,2006; 26(6):33) |
| [8] | Keanini R G,Rubinsky B.Int J Heat Mass Transfer,1993;36:3283 |
| [9] | Nehad A K.Int Commun Heat Mass,1995; 22:779 |
| [10] | Wu C S,Wang H G,Zhang Y M.Weld J,2006; 85:284s |
| [11] | Wu C S,Hu Q X,Gao J Q.Comp Mater Sci,2009; 46:167 |
| [12] | Huo Y S,Wu C S.China Weld,2009; 18(3):12 |
| [13] | Fan H G,Kovacevic R.J Phys,1999; 32D:2902 |
| [14] | Wu C S. Welding Thermal Processes and Weld Pool Behaviors.Boca Raton: CRC Press/Taylor & Francis Group,2010:49 |
| [15] | Wu C S,Chen J,Zhang Y M.Comp Mater Sci,2007; 39:635 |
| [16] | Sahoo P,Debroy T,Mcnallan M J.Metall Mater Trans,1988; 19B:483 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%