采用3种应变速率在不同温度下对一种奥氏体铁镍基合金进行拉伸实验,结果发现在300-700℃范围内发生锯齿流变现象；锯齿流变现象在300-600℃范围内表现为凸起式锯齿,而在700℃时表现为下凹式锯齿；此锯齿流变具有热激活性,即较高的拉伸温度使锯齿易于发生,较大的拉伸速率则抑制其发生.对比分析室温(不发生锯齿流变)及400℃(显著发生锯齿流变)拉伸试样的微观组织,发现在400℃拉伸后的孪晶界上存在明显的位错塞积,说明孪晶界可以有效地阻碍滑移变形,引起孪晶界附.近应力积累,从而导致了凸起式锯齿流变的发生.孪晶界数量对锯齿波形的影响证实了此观点.
参考文献
| [1] | Le Chatelier A.Rev de Metall,1909; 6:914 |
| [2] | Zeides F,Roman I.Scr Metall,1990; 24:1919 |
| [3] | Zavattieri P D,Savic V,Hector Jr L G,Fekete J R,Tong W,Xuan Y.Int J Plast,2009; 25:2298 |
| [4] | Jiang H F,Zhang Q C,Yu Y H,Wu X P.Acta Metall Sin,2006; 42:139(江慧丰,张青川,徐毅豪,伍小平.金属学报,2006; 42:139) |
| [5] | Fournier L,Savoie M,Delafosse D.J Nucl Mater,2007;366:187 |
| [6] | Cottrell A H.Philos Mag,1953; 44:829 |
| [7] | Zhu S M,Nie J F.Scr Metall,2004; 50:51 |
| [8] | Prasad K,Varma V K.Mater Sci Eng,2008; A486:158 |
| [9] | Hale C L,Rollings W S,Weaver M L.Mater Sci Eng,2001; A300:153 |
| [10] | Shields J A,Goods S H,Gibala R,Mitchell T E.Mater Sci Eng,1975; A20:71 |
| [11] | Basinski Z S.Aust J Phys,1960; 13:354 |
| [12] | Onodera R,Era H,Ishibash T,Shimizu M.Acta Metall,1983; 31:1589 |
| [13] | Li X Y,Zhang J,Rong L J,Li Y Y.J Alloys Compd,2009;467:383 |
| [14] | Michiuchi M,Kokawa H,Wang Z J,Sato Y S,Sakai K.Acta Metall,2006; 54:5179 |
| [15] | Mahajan S,Chin G Y.Acta Metall,1973; 21:173 |
| [16] | Rémy L.Acta Metall,1977; 25:711 |
| [17] | Jin Z H,Gumbsch P,Albe K,Ma E,Lu K,Gleiter H,Hahn H.Acta Mater,2008; 56:1126 |
| [18] | Qu S,Zhang P,Wu S D,Zang Q S,Zhang Z F.Scr Metall,2008; 59:1131 |
| [19] | Pémy L.Acta Metall,1977; 25:173 |
| [20] | Nembach E.Mater Sci Eng,2006; A429:277 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%