采用粉末冶金梯级烧结法成功制备出轻质、高强且具有一定孔隙率的纳米SiC颗粒增强NiTi合金基形状记忆复合材料(SiC/NiTi).研究发现,所制备的SiC/NiTi复合材料具有稳定的线性超弹性;SiC颗粒的引入使SiC/NiTi复合材料具有较高的压缩强度和等效压缩强度,且强度随SiC含量的增加而提高.研究还表明,SiC颗粒对合金相组成有一定影响,但复合材料仍具有NiTi合金的马氏体转变特征,并保持NiTi合金的高阻尼特性及较高的存储模量.
参考文献
[1] | Miyazaki S,Otsuka K.Trans ISIJ,1989; 29:353 |
[2] | Graesser E J,Cozzarelli F A.J Eng Mech,1991; 117:2590 |
[3] | Aiken I D,Nims K D,Whittaker A S,James M K,Eeri M.Earthq Spectra,1993; 9:335 |
[4] | Van Humbeeck J.J Alloys Compd,2003; 355:58 |
[5] | Li D S,Zhang Y P,Xiong Z P,Zhang X P.Acta Metall Sin,2008; 44:995(李大圣,张宇鹏,熊志鹏,张新平.金属学报,2008;44:995) |
[6] | Li B Y,Rong L J.J Mater Res,1998; 13:2847 |
[7] | Yuan B,Chung C Y,Zhang X P,Zeng M Q,Zhu M.Smart Mater Struct,2005; 14:S201 |
[8] | Zhang Y P,Li D S,Zhang X P.Scr Mater,2007; 57:1020 |
[9] | Yang Y,Lan J,Li X C.Mater Sci Eng,2004; A386:284 |
[10] | Li D S,Zhang X P,Xiong Z P,Mai Y W.J Alloys Compd,2010; 490:15 |
[11] | Maruyama B,Hunt W.JOM,1999; 11:59 |
[12] | Contreras A,Angeles-Chávez C,Flores O,Perez R.Mater Charact,2007; 58:685 |
[13] | Zhang Y P,Yuan B,Zcng M Q,Chung C Y,Zhang X P.J Mater Process Technol,2007; 439:192 |
[14] | Kuang Y H,Ngai T,H G,Li Y Y.J Alloys Compd,2009;209:4607 |
[15] | Gale W F,Totemeier T C.Smithell Metals Reference Book.Netherlands:Elsevier,2004:9 |
[16] | Ke C B,Ma X,Zhang X P.Acta Metall Sin,2011; 47:129(柯常波,马骁,张新平.金属学报,2011:47:129) |
[17] | Rao G B,Wang J Q,Han E H,Ke W.Acta Metall Sin,2002; 38:575(饶光斌,王俭秋,韩恩厚,柯伟.金属学报,2002; 38:575) |
[18] | Zhang X P,Liu H Y,Yuan B,Zhang Y P.Mater Sci Eng,2008; A481:170 |
[19] | Li D S.PhD Thesis,South China University of Technology,Guangzhou,2009(李大圣.华南理工大学博士论文,广州,2009) |
[20] | Zhao J S.The Basis of Dislocation Theory.Beijing:National Defense Industry Press,1989:148(赵敬世.位错理论基础.北京:国防工业出版社,1989:148) |
[21] | Lin H C,Wu S K,Yeh M T.Metall Mater Trans,1993;24A:2189 |
[22] | Nishiyama K,Yamanaka M,Omori M,Umekawa S.Mater Sci Lett,1990; 9:526 |
[23] | Gao M X,Oliveira F J,Pan Y,Yang L,Baptista J L,Vieira J M.Intermetallics,2005; 13:406 |
[24] | Wang H M,Wang C M,Cai L X.Surf Coat Technol,2003;168; 202 |
[25] | Cai W,Lu X L,Zhao L C.Mater Sci Eng,2005; A394:78 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%