本文对化学剂冷却热轧螺纹钢在两段式冷却(前段化学剂FM冷却+后段水冷)过程中的温度场进行了有限元模拟,并在实验室对前段化学剂FM冷却生成的氧化皮的耐蚀性能进行了评价.采用工业现场一段式水冷的工艺参数,模拟了一段式水冷的温度场.对比一段式水冷的温度场,分析了两段式冷却的工艺参数对冷却过程温度场的影响.结果表明,在前段化学剂FM冷却时,采用较小的对流换热系数,有利于提高前段化学剂冷却时的氧化温度,从而改善氧化皮的质量；在后段水冷时,在保持原一段水冷的对流换热系数的情况下,两段式冷却水冷段的冷却曲线与一段式水冷非常接近,能够满足Ⅲ级热轧螺纹钢的力学性能的要求.采用有限元模拟优化的工艺参数,在实验室模拟了前段化学剂FM冷却过程,获得了致密的氧化皮,其耐蚀性能显著优于水冷钢筋,说明采用前段化学剂冷却来改善水冷钢筋的耐蚀性能是可行的.
参考文献
| [1] | Pradhan B,Bhattacharjee B.Constr Build Mater,2011;25:2565 |
| [2] | Shi X M,Ning X,Keith F,Jing G.Constr Build Mater,2012; 30:125 |
| [3] | Zhao M Q,Zhang R Q,Yang Z,Li G J.Anhui Metall,2003; 4:23(赵明琦,张若蔷,杨峥,李光俊.安徽冶金,2003;4:23) |
| [4] | Huang W,Zhang L,Wang p,Shu W.Archit Technol,2010;41:242(黄伟,张丽,王平,疏伟.建筑技术,2010; 41:242) |
| [5] | Nikolaou J,George D P.Int J Impact Eng,2005; 31:1065 |
| [6] | Li G F,Dong H,Gao W,Zhao Y J.J Iron Steel Res,1996;8:42(李桂芬,董瀚,高伟,赵玉君.钢铁研究学报,1996;8:42) |
| [7] | Sun X W,Huo X D,Liu D L,Kang Y L,Mao X P,Chen G J,Li L Y.J Univ Sci Technol Beijing,2004; 26:268(孙贤文,霍向东,柳得橹,康永林,毛新平,陈贵江,李烈军.北京科技大学学报,2004; 26:268) |
| [8] | Zakya A I,E1 Morsyb A,El-Bitar T.J Mater process Technol,2009; 209:1565 |
| [9] | Wei J,Dong J H,Han E H,Ke W.Corros Sci Prot Technol,2009; 21:468(魏洁,董俊华,韩恩厚,柯伟.腐蚀科学与防护技术,2009;21:468) |
| [10] | Zitrou E,Nikolaou J,Tsakiridis P E,Papadimitriou G D.Constr Build Mater,2007; 21:1161 |
| [11] | Castro P,Wéleva L,Balancán M.Constr Build Mater,1997; 11:75 |
| [12] | Novak P,Mala R,Joska.L.Cem Concr Res,2001; 31:589 |
| [13] | Zou Y,Wang J,Zheng Y Y.Corros Sci,2011; 53:208 |
| [14] | Wei J,Dong J H,Ke W.Constr Build Mater,2010; 24:275 |
| [15] | Wei J,Dong J H,Ke W.Constr Build Mater,2011; 25:1243 |
| [16] | Chen R Y,Yuen W Y D.Oxid Met,2001; 56:89 |
| [17] | Almusallam A A.Constr Build Mater,2001; 15:361 |
| [18] | Pérez F J,Martínez L,Hierro M P,Gómez G,Portela A L,Pucci G N,Duday D,Lecomte-Beckers J,Greday Y.Corro Sci,2006; 48:472 |
| [19] | Saurabh K,Ananya M,Sudin C,Sanjay C.ISIJ Int,2004;44:1217 |
| [20] | Cheng M,Hong H P,Peng D,Kang Y L,Jin Y C.J Iron Steel Res,2008; 20:18(程满,洪慧平,彭聃,康永林,金永春.钢铁研究学报,2008;20:18) |
| [21] | Lee Y Y,Choi S,Hodgson P D.Mater Process Technol,2002; 125:678 |
| [22] | Morales R D,Lopez A G,Olivare M.ISIJ Int,1990; 30:48 |
| [23] | Yao S C,Cox T L.Exp Heat Transfer,2002; 15:207 |
| [24] | Zhang G B,Sheng Y,Wei M J,Wu X Z,Wang Y S,Liu Q L.J Heibei Inst Technol,2002; 24:32(张国滨,盛艳,魏明军,武学泽,王彦生,刘庆禄.河北理工学院学报,2002:24:32) |
| [25] | Freund S,Pautsch A G,Shedd T A,Kabelac S.Int J Heat Mass Transfer,2007; 50:1953 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%