对Fe52Co34Hf7B6Cu1非晶合金进行了低频磁脉冲处理,研究低温真空退火对磁脉冲处理Fe52Co34Hf7B6Cu1非晶软磁性能的影响.结果表明,磁脉冲处理导致非晶合金发生纳米晶化,析出晶态相α-Fe(Co),晶粒尺寸为5-10nm,形成的纳米晶粒弥散分布于非晶基体的双相纳米合金中.对磁脉冲处理的试样进行低温真空退火,可以进一步优化纳米合金的软磁性能,在100℃退火可以得到最佳的软磁性能.
参考文献
| [1] | Kowalczyk M,Ferenc J,Liang X B,Kulik T.J Magn Magn Mater,2006; 04:e651 |
| [2] | Liang X B,Ferenc J,Kulik T,Xu B S.Mater Sci Eng,2006; A426:169 |
| [3] | Liang X B,Kulik T,Ferenc J,Kowalczyk M,Vlasak G,Sun W S,Xu B S.Physica,2005; 370B:151 |
| [4] | Kulik T,Liang X B,Ferenc J,Xu B S.Surf Eng China,2004; 68:1.(Kulak T,梁秀兵,Ferenc J,徐滨士.中国表面工程,2004; 68:1) |
| [5] | Blazquez J S,Franco V,Conde C F,Conde A,Ferenc J,Kulik T.J Non-Cryst Solids,2007; 353:872 |
| [6] | Xiao S H,Chao Y S,Zhou B L.Acta Phys Sin,2000; 49:288.(肖素红,晁月盛,周本濂,物理学报,2000; 49:288) |
| [7] | Chao Y S,Li M Y,Geng Y,Liu J G.Acta Phys Sin,2004;53:3453.(晁月盛,李明扬,耿岩,刘吉刚.物理学报,2004; 53:3453) |
| [8] | Chao Y S,Zhang Y H,Guo H,Zhang L,Wang X G.Acta Metall Sin,2007; 43:231.(晁月盛,张艳辉,郭红,张莉,王兴刚.金属学报,2007; 43:231) |
| [9] | Chao Y S,Zhu H X,Li Z M.J Phys,2009; 188:012038 |
| [10] | Kopcewicz M,Gonser U,Wagner H G.Appl Phys,1980;23:1 |
| [11] | Kopcewicz M,Wagner H G,Gonser U.J Magn Magn Mater,1983; 40:139 |
| [12] | Majumdar B,Bysak S,Akhtar D.J Magn Magn Mater,2007; 309:300 |
| [13] | Chao Y S,Guo H,Gao X Y,Luo L P,Zhu H X.Acta Phys Sin,2011; 60:017504.(晁月盛,郭红,高翔宇,罗丽平,朱涵娴.物理学报,2011; 60:017504) |
| [14] | Sato K,Murakami H,Kobayashi Y,Sprengel W,Schaefer H E.J Non-Cryst Solids,2007; 353:1882 |
| [15] | Tian S.Physical Properties of Materials.Beijing:Aviation and Aerospace University Press,2000:265.(田莳.材料物理性能.北京:北京航空航天大学出社,2000:265) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%