以溶质原子为中心,并在第一配位壳层堆垛不同原子,构造了一个新的原子密堆垛模型,用于预测像高溶质浓度Ti-Ni-Al等(伪)三元合金体系中玻璃形成能力最佳的合金.此模型不仅在Ti-Ni-Al,Ti-Ni-Sn等具有条带玻璃形成能力的三元体系中,而且在其它一些具有块体玻璃形成能力的体系中对玻璃形成能力最佳的合金成分预测结果与实验结果吻合良好.
参考文献
| [1] | Inoue A,Nishiyama N,Kimura H.Mater Trans JIM,1997;38:179 |
| [2] | Inoue A,Zhang T.Mater Trans JIM,1996; 37:185 |
| [3] | Ma H,Shi L L,Xu J,Li Y,Ma E.Appl Phys Lett,2005;87:181915 |
| [4] | Guo F Q,Wang H J,Poon S J,Shiflet G J.Appl Phys Lett,2005; 86:091907 |
| [5] | Turnbull D.Contemp Phys,1969; 10:473 |
| [6] | Inoue A.Acta Mater,2000; 48:279 |
| [7] | Lu Z P,Liu C T.Acta Mater,2002; 50:3501 |
| [8] | Lisboa R D S,Bolfarini C,Botta W J F,Kiminami C S.Appl Phys Lett,2005; 86:211904 |
| [9] | Miracle D B.Nat Mater,2004; 3:697 |
| [10] | Wang A P,Wang J Q,Ma E.Appl Phys Lett,2007; 90:121912 |
| [11] | Shi L L,Xu J,Ma E.Acta Mater,2008; 56:3613 |
| [12] | Lü B C,Yao J H,Xu J,Li Y.Appl Phys Lett,2009; 94:241913 |
| [13] | Pelton A D,Degterov S A,Erksson G,Robelin C,Dessureault Y.Metall Mater Trans,2000; 31B:651 |
| [14] | Guo F Q,Poon S J,Shiflet G J.J Appl Phys,2004; 97:013512 |
| [15] | Miracle D B.J Non-Cryst Solids,2004; 342:89 |
| [16] | Miracle D B,Sanders W S,Senkov O N.Philos Mag,2003;83:2409 |
| [17] | Senkov O N,Scott J M.Scr Mater,2004; 50:449 |
| [18] | Miracle D B.Acta Mater,2006; 54:4317 |
| [19] | Lü B C,Li Y,Xu J.J Alloys Compd,2009; 467:261 |
| [20] | Lü B C,Xu J.J Non Cryst Solids,2008; 354:5425 |
| [21] | Jing Q,Zhang Y,Wang D,Li Y.Mater Sci Eng,2006;A441:106 |
| [22] | Zhang T,Inoue A.Mater Trans,1998; 39:1001 |
| [23] | Inoue A K,Nishiyama N K,Matsuda T K.Mater Trans,1996; 37; 181 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%