利用热模拟试样模拟TiNi合金激光焊接接头焊缝热影响区,对焊接接头、焊缝金属、模拟热影响区和母材的相变温度进行差热分析,研究了焊接接头与其它三者逆相变温度的关系,并利用OM,SEM和XRD对母材、热影响区和焊缝金属的组织、析出相的分布以及晶体结构进行了研究.结果表明,TiNi合金激光焊接接头的形状恢复率与母材无明显差别,但形状恢复温度区间与母材差异较大,其形状恢复开始温度比母材低40℃；焊缝金属和热影响区逆相变开始温度(As)和结束温度(Af)均不同于母材,主要原因是焊缝金属经历了熔化-凝固过程,失去了母材中原有的晶体择优取向,且析出相尺寸小,分布不均；而热影响区As和Af降低,可能是细小析出相重新固溶于基体所致,整个接头的逆相变温度区间与焊缝金属近似,调控焊缝金属的相变温度是控制TiNi合金激光焊接接头形状记忆功能的关键.
参考文献
| [1] | Zhao L C,Cai W,Zheng Y F.Shape Memory Effect and Superelasticity in Alloys. Beijing:National Defense Industry Press,2002:5(赵连成,蔡伟,郑玉峰.合金的形状记忆效应和超弹性.北京:国防工业出版社,2002:5) |
| [2] | Xu Z Y.Shape Memory Materials.Shanghai:Shanghai Jiao Tong University Press,2002:18(徐祖耀.形状记忆材料.上海:上海交通大学出版社,2002:18) |
| [3] | Funakubo H,translate by Qian D F.Shape Memory Alloys.Beijing:China Machine Press,1984:85(Funakubo H著,千东范 译.形状记忆合金.北京:机械工业出版社,1984:85) |
| [4] | Otsuka K,Mayman C M.Shape Memory Materials.Cambridge:Cambridge University Press,1998:49 |
| [5] | Yang J,Wu Y H.Shape Memory Alloys and Their Applications.Hefei:Chinese Science and Technology University Press,1993:36(杨杰,吴月华.形状记忆合金及其应用.合肥:中国科学技术大学出版社,1993:36) |
| [6] | Ren J L,Wu A P.Joining of Advanced Materials.Beijing:China Machine Press,2000:335(任家烈,吴爱萍.先进材料的连接,北京:机械工业出版社,2000:335) |
| [7] | Ikai A,Kimura K,Tobushi H.J Intell Mater Syst Struct,1996; 7:646 |
| [8] | Tuissi A,Besseghini S,Ranucci T,Squatrito F,Pozzi M.Mater Sci Eng,1999; A273-275:813 |
| [9] | Hsu Y T,Wang Y R,Chen C.Metall Mater Trans,2001;32A:569 |
| [10] | Falvo A,Furgiuele F M,Maletta C.Mater Sci Eng,2005;A412:235 |
| [11] | Xu Y L,Cheng Z F,Fan X L,Chu C L,Wang S D.Trans Chin Weld Inst,2006; 27:26(徐越兰,成志富,范晓龙,储成林,王世栋.焊接学报,2006; 27:26) |
| [12] | Falvo A,Furgiuele F M,Maletta C.Mater Sci Eng,2008;A481-482:647 |
| [13] | Barcellona A,Fratini L,Palmeri D,Maletta C,Brandizzi M.Int J Mater Form,2010; 3:1047 |
| [14] | Yang C G,Shah J G,Wen P,Ren J L.Acta Metall Sin,2011; 47:1277(杨成功,单际国,温鹏,任家烈.金属学报,2011,47:1277) |
| [15] | Xie C Y,Zhao L C,Lei T Q.Acta Aeronaut Astronaut Sin,1991; 12:A395(谢超英,赵连成,雷廷权.航空学报,1991:12:A395) |
| [16] | Xie C Y,Zhao L C,Lei T Q.Met Sci Technol,1990; 9:118(谢超英,赵连成,雷廷权.金属科学与工艺,1990;9:118) |
| [17] | Michutta J,Somsen C,Yawny A,Dlouhy A,Eggeler G.Acta Mater,2006; 54:3525 |
| [18] | Fan G,Chen W,Yang S,Zhu J,Ren X,Otsuka K.Acta Mater,2004; 52:4351 |
| [19] | Huang Y S,Lin G M,Lai Q L.Chin J Nonferrous Met,1993; 3:57(黄元士,林光明,赖奇略.中国有色金属学报,1993;3:57) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%