研究了Ni-Cr-Mo-B超厚钢板表面低碳回火马氏体组织.对表面区域不同位置处取样进行了冲击性能测试,并借助OM,SEM,EBSD,XRD和正电子湮没谱(PAS)等技术手段对马氏体组织及其亚结构进行了研究.结果表明,实验钢表面韧性异常恶化,马氏体组织中相对粗大的板条束和板条块以及较高的位错密度是其表面韧性恶化的主要原因.
参考文献
| [1] | Dong T.Wide Heavy Plate,1995; 1(3):1(东涛.宽厚板,1995:1(3):1) |
| [2] | Tang X S.Mar Equip Mater Mark,2010; 1:10(唐学生.船舶物资与市场,2010;1:10) |
| [3] | Di G B,Liu Z Y,Hao L Q,Liu X H.Mater Mech Eng,2008; 32(8):1(狄国标,刘振宇,郝利强,刘相华.机械工程材料,2008;32(8):1) |
| [4] | Li R P,Xie Y H,Shu Z.China Offshore Platform,2003;18(3):1(李润培,谢永和,舒志.中国海洋平台,2003:18(3):1) |
| [5] | Chen A Z,Niu J C,Deng W P.Develop Appl Mater,2010;25(1):9(陈爱志,牛继承,邓晚平.材料开发与应用,2010;25(1):9) |
| [6] | Wang R F,Xu K,Xue G.Hot Work Technal,2007; 36(16):43(王任甫,徐科,薛钢.热加工工艺,2007; 36(16):43) |
| [7] | Luo Z J,Shen J C,Su H,Ding Y H.Develop Appl Mater,2009; 24(5):1(罗志俊,沈俊昶,苏航,丁跃华.材料开发与应用,2009; 24(5):1) |
| [8] | Xu Z Y.Martensite and Martensite Transformation.2nd Ed.,Beijing:Science Press,1999:213(徐祖耀.马氏体与马氏体相变.第2版,北京:科学出版社,1999:213) |
| [9] | Tomita Y,Okabayashi K.Metall Trans,1986; 176A:1203 |
| [10] | Wang C F,Wang M Q,Shi J,Dong H.Scr Mater,2008;58:492 |
| [11] | Inoue T,Matsuda S,Okamura Y.Trans JIM,1970; 11:36 |
| [12] | Luo Z J,Shen J C,Su H,Ding Y H,Yang C F,Zhang Y Q,Ma Y.Trans Mater Heat Treat,2010; 31(10):63(罗志俊,沈俊昶,苏航,丁跃华,杨才福,张永权,马跃.材料热处理学报,2010; 31(10):63) |
| [13] | Park Y K,Waber J T.Mater Lett,1985; 3:181 |
| [14] | Shirai Y,Araki H,Mori T,Nakamura W,Sakaki K.J Alloys Compd,2002; 330-333:125 |
| [15] | Kuramoto E,Tsutsumi T,Ueno K,Ohmura M,Kamimura Y.Comput Mater Sci,1999; 14:30 |
| [16] | Eldrup M.J Phys Ⅳ,1995; 5(C1):93 |
| [17] | Mohamed H F M,Kwon J,Kim Y M,Kim W.Nucl Instrum Methods Phys Res,2007; 258B:429 |
| [18] | Wu Y C,Zhu Z Y,Itoh Y,Ito Y.Nucl Tech,1998; 21:135(吴奕初,朱梓英,伊东芳子,伊藤泰男.核技术,1998; 21:135) |
| [19] | Wang S J,Wu Y C,Chen Z Q,Fang P F,Wang B,Zhang Y X.Applied Positron Spectroscopy.Wuhan:Hubei Science and Technology Press,2008:77(王少阶,吴奕初,陈志权,方鹏飞,王波,张永学.应用正电子谱学.武汉:湖北科学技术出版社,2008:77) |
| [20] | Masumoto I,Suga H.J Jpn Weld Soc,1982; 51:586(益本功,须賀久明.溶接学会誌,1982:51:586) |
| [21] | Liu Y M.J Iron Steel Res,2007; 19(4):1(刘禹门.钢铁研究学报,2007; 19(4):1) |
| [22] | Yong Q L.Secondary Phasesin Steels.Beijing:Metallurgical Industry Press,2006:37(雍岐龙.钢铁中的第二相.北京:冶金工业出版社,2006:37) |
| [23] | Mandziej S T.Mater Sci Eng,1993; A164:275 |
| [24] | Cottrell A H.Trans Met Soc AIME,1958; 212:192 |
| [25] | Cottrell A H.Fracture.New York:Technology Press MIT and John Wiley,1959:20 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%