为揭示磁脉冲成形的增塑机制,采用理论分析与微观组织观察相结合的方法对5052铝合金板材磁脉冲动态拉伸过程中动态成形行为和塑性失稳机制进行了系统研究.结果表明,惯性力在动态成形中起主要作用,惯性力对试样的结构失稳具有抑制作用,从而使试样的塑性提高并产生分散失稳；5052铝合金动态成形和准静态成形的成形性质相似,不会产生特殊的组织结构,塑性变形机制均为位错滑移机制；准静态成形过程以均匀单系位错滑移为主,断裂伴随着位错的缠结和攀移；而动态成形过程中,位错滑移趋于多系开动,在大面积区域出现明显的交滑移现象,且滑移带较准静态成形时窄且密,位错组态更均匀；动态成形的多系滑移和位错均化作用可在比准静态成形高的多的塑性应变水平下形成,从而使材料表现出较高的塑性和强度.
参考文献
| [1] | Li C F.High Energy Rate Forming. Beijing:National Defense Industry Press,2001:1(李春峰.高能率成形技术.北京:国防工业出版社,2001:1) |
| [2] | Psyk V,Risch D,Kinsey B L,Tekkaya A E,Kleiner M.J Mater Process Technol,2011; 5:787 |
| [3] | Vohnout V J.PhD Thesis,Ohio State University,Columbus,1998 |
| [4] | Balanethiram V S,Daehn G S.Scr Metall,1992; 27:1783 |
| [5] | Balanethiram V S,Daehn G S.Scr Metall,1994; 30:515 |
| [6] | Balanethiram V S,Hu X Y,Daehn G S.J Mater Process Technol,1994; 45:595 |
| [7] | Hu X Y,Wagoner R H,Daehn G S,Ghosh S.Metall Trans,1994; 25A:2723 |
| [8] | Hu X Y,Daehn G S.Acta Mater,1996; 44:1021 |
| [9] | Oliveira D A,Worswick M J.J Phys Ⅳ France,2003; 110:293 |
| [10] | Oliveira D A,Worswick M J,Finn M,Newman D.J Mater Process Technol,2005; 170:350 |
| [11] | Imbert J M,Winkler S L,Worswick M J,Oliveira D A.J Eng Mater Technol,2005; 27:127 |
| [12] | Seth M.PhD Thesis,Ohio State University,Columbus,2006 |
| [13] | Thomas J D,Seth M,Daehn G S,Bradley J R,Triantafyllidis N.Acta Mater,2007; 55:2863 |
| [14] | Regazzoni G,Kocks U F,Follansbee P S.Acta Mater,1987; 35:2865 |
| [15] | Follansbee P S,Kocks U F.Acta Mater,1988; 36:81 |
| [16] | Gorham D A.J De Phys Ⅲ 1991; 1:411 |
| [17] | Dioh N N,Leevers P S,Williams J G.Polymer,1993; 34:4230 |
| [18] | Meyers M A.Dynamic Behavior of Materials.New York:Wiley,1994 |
| [19] | Golovashchenko S F.J Mater Eng Perform,2007; 16:314 |
| [20] | Hecker S S.J Eng Mater Technol,1975; 97H:66 |
| [21] | Blazynsk T Z,translated by Li F Q,Wu B Q.Explosive Welding,Forming and Compaction.Beijing:China Machine Press,1983:76(Blazynsk T Z著,李富勤,吴柏青 译.爆炸焊接、成形与压制.北京:机械工业出版社,1983:76 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%