用TEM,OM,SEM和Vickers硬度仪测定、表征了铸态.同溶+时效态下不同La含量AZ91合金的显微组织和析出相的形态和尺寸以及硬度变化,研究了不连续β柑和Al11La3相的形貌对合金硬度的影响及其机理,并计算时效过程中Al原子的扩散系数.结果表明,不同 La含量AZ91合金在170℃时,La含量为0.16％的合金时效24h达到的硬度最大,为138HV;延长时效时间和改变La含量可使不连续脱溶相转变为板条状连续脱溶相,降低Al原子的扩散系数,从而影响不连续β相的数量,大小与分布；晶界处的Al11La3相的形貌虽不受热处理过程影响,但却制约β相的长大.可见控制La含量和时效时间,可改善不连续(片层)β相的尺寸和数量,有效地提高合金强韧性能.
参考文献
| [1] | Aghion E,Bronfin B,Eliezer D.J MaterProcess Technol,2001; 117:381 |
| [2] | Mordike B L,Ebert T.Mater Sci Eng,2001; A302:37 |
| [3] | Liu Q.Acta Metall Sin,2010; 46:1458(刘庆.金属学报,2010; 46:1458) |
| [4] | Chen Z H,Yan H G.Magnesium Alloy.Beijing:Chemical Industry Press,2004,29(陈振华,严红革镁合金北京化学工业出版社,2004,29) |
| [5] | Clark J B,Zabdyr L,Moser Z.Ins ASM Handbook,vol.3,Alloy Phose Diagrama.Materials Park,Ohio:ASM International,1992:285 |
| [6] | Zeng X Q,Wu Y J,Peng L M.Aeta Metall Sin,2010; 46:1041(曾小勤,吴玉娟,彭立明金属学报,2010; 46:1041) |
| [7] | Xiao X L,Luo C P,Liu J W,Wu D X,Nie J F.Chin J Nonferrous Met,2003; 13:15(肖晓玲,罗承萍,刘江文,吴东晓,聂建峰.中国有色金属学报,2003; 13:15 |
| [8] | Xiao X L,Luo C P,Nie J F.Acta Metall Sin,2001; 37:1(肖晓玲,罗承萍,聂建峰金属学报,2001; 37:1) |
| [9] | Xiao X L,Luo C P,Liu J W,Nie J F.Acta Metall Sin,2002; 28:709(肖晓玲,罗承萍,刘江文,聂建峰.金属学报,2002; 28:709) |
| [10] | Cizek L,Greger M,Pawlica L,Dobrzanski L A,Tanski T.J Mater Process Technol,2004; 157-158:466 |
| [11] | Li P J,Tang B,Kandal ova E G.Mater Lett,2005; 59:671 |
| [12] | Zhao Y H,Chen Y G,Tang Y B.Rare Met Mater Eng,2010; 39:843(赵源华,陈云贵,唐永柏.稀有金属材料与工程,2010; 39:844) |
| [13] | Zhang J L,Wang S B,Xu B S.Rare Met Mater Eng,2007;30:1061(张金玲,王社斌,许并社.稀有金属材料与工程,2007; 36:1061) |
| [14] | Li W X.Magnesium and Magnesium Alloy. Changsha:Central South University Prees,2005; 341(黎文献.镁及镁合金.长沙:中南大学出版社,2005,341) |
| [15] | Tang W,Han E H,Xu Y B.Acta Metall Sin,2005,41:1199(唐伟,韩恩厚,徐永波.金属学报,2005; 41:1199) |
| [16] | Zhang J M,Jiang B L,Wang Z H,Yuan S,Xia P J.Heat Treat Met.2007; 32:6(张菊梅,蒋百灵,王志虎,袁森,夏鹏举.金属热处理,2007;32:6) |
| [17] | Wang S B,Qi X Y,Zhang J L,Xu B S.Acta Metall Sin,2011; 47:743(王社斌,祁小叶,张金玲,许并社.金属学报,2011:47:743) |
| [18] | Wu Y R.PhD Thesis,Hunan University,Changsha,2007(吴玉蓉.湖南大学博士论文,长沙,2007) |
| [19] | Liu L F,Ding H L,Ding W J.Rare Met Mater Eng,2009;38:104(刘六法,丁汉林,丁文江.稀有金属材料与工程,2009; 38:104) |
| [20] | Yu K,Li W X,Zhang S J.Rare Met Mater Eng,2005; 34:1105(余琨,黎文献,张世军.稀有金属材料与工程,2005;34:1105) |
| [21] | Wang S B,Zhang J L,Qi X Y,Xu B S.Mater Eng,2009;(Suppl.1):303(王社斌,张金玲,祁小叶,许并社.材料工程,2009;(增刊1):303) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%