以传统TWIP钢为对比,测试了含NTWIP钢的力学性能,并利用XRD进行物相分析和TEM进行微观结构表征.结果表明,在由fcc或hcp结构向bcc结构马氏体进行相变时,晶体结构中的最大间隙由0.1047nm降低至0.0725nm.间隙原子N的存在显著增大bcc结构的晶格畸变能,提高α马氏体切变的阻力,因而强烈抑制α马氏体相变,导致组织中hcp结构ε相含量大幅度增加,提高了TWIP钢的强度,但也降低了钢的塑性,另外,奥氏体平均和区域层错几率的计算及微观组织分析结果表明,形变增加层错的数量,而马氏体相变消耗层错,从而减少层错数量.
参考文献
| [1] | Grassel O,Frommeyer G,Derder C,Hofmann H.J Phys Ⅳ France,1997;5:383 |
| [2] | Frommeyer G,Brux U,Neumann P.ISIJ Int,2003;43:438 |
| [3] | Vercammen S,Blanpain B,De Cooman B C,Wollants P.Acta Mater,2004;52:2005 |
| [4] | Sato K,Ichinose M,Hirotsu Y,Inoue Y.ISIJ Int,1989;29:868 |
| [5] | Christian J W,Mahajan S.Prog Mater Sci,1995;39:1 |
| [6] | Grassel O,Kruger L,Frommeyer G,Meyer L W.Int J Plasticity,2000;16:1391 |
| [7] | Schramm R E,Reed R P.Metall Trans,1975;6A:1345 |
| [8] | Yakubtsov I A,Ariapour A,Perovic D D.Acta Mater,1999;47:1271 |
| [9] | Wan J F,Huang X,Chen S P,Hsu T Y(Xu Z Y).Mater Trans JIM,2002;43:920 |
| [10] | Wan J F,Chen S P,Hsu T Y(Xu Z Y).Acta Metall Sin,2000;36:679(万见峰,陈世朴,徐祖耀.金属学报,2000;36:679) |
| [11] | Huang B X,Wang X,Wang L,Rong Y.Metall Mater Trans,2008;39A:717 |
| [12] | Huang B X.PhD Thesis,Shanghai Jiaotong University,2007(黄宝旭.上海交通大学博士论文,2007) |
| [13] | Huang X,Wan J F,Chen S P,Hsu T Y(Xu Z Y).J Shanghai Jiaotong Univ,2002;36:21(黄幸,万见峰,陈世朴,徐祖耀.上海交通大学学报,2002;36:21) |
| [14] | Fan X.Metal X-ray Analysis.Beijing:China Machine Press,1996:36(范雄.金属X射线学.北京:机械工业出版社,1996:36) |
| [15] | Zuo Y S,Chen W Z,Liang W.Modern Methods of Materials Testing.Beijing:Beijing University of Technology Press,2000:101(左演声,陈文哲,梁伟.材料现代分析方法.北京:北京工业大学出版社,2000:101) |
| [16] | Rong Y H,He G,Guo Z H,Chen S P,Hsu T Y(Xu Z Y).J Mater Sci Technol,2002;18:459 |
| [17] | Nishiyama Z,Kakinoki J,Kajiwara S.J Phys Soc Jpn,1965;20:1192 |
| [18] | Kajiwara S.J Appl Phys,1970;9:385 |
| [19] | Kajiwara S.J Phys Soc Jpn,1967;22:795 |
| [20] | Wang X D,Huang B X,Rong Y H,Wang L.J Appl Phys,2007;101:093511 |
| [21] | Pan J S,Tong J M,Tian M B.Fundamental of Materials.Beijing:Tsinghua University Press,2002:18(潘金生,仝健民,田民波.材料科学基础.北京:清华大学出版社,2002:18) |
| [22] | Yang F J.Atomic Physics.Beijing:Higher Education Press,1985:509(杨福家.原子物理学.北京:高等教育出版社,1985:509) |
| [23] | Jiang B,Qi X,Yang S,Yang S,Zhou W,Hsu T Y(Xu Z Y).Acta Mater,1998;46:501 |
| [24] | Warren B E.X-ray diffraction.Massachusett:Addison Wesley,1969:275 |
| [25] | Hsu T Y(Xu Z Y).Acta Metall Sin,1980;16:430(徐祖耀.金属学报,1980;16:430) |
| [26] | Hsu T Y(Xu Z Y).Martensitic Transformation and Martensite.Beijing:Science Press,1999:83(徐祖耀.马氏体相变与马氏体.北京:科学出版社,1999:83) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%