使用Nd3+:YAG脉冲激光器产生的脉冲能量为12.5J,频率10 Hz,波长1064 nm的脉冲激光研究了强激光冲击下的Ti-6Al-4V合金表面响应,用SEM和TEM及IFFT方法分析了激光冲击强化造成的微结构响应.结果表明,激光冲击可使Ti-6Al-4V合金表面硬度增加80％以上,残余压应力达到500 MPa以上.在激光冲击产生的超高能量和超高应变率作用下,具有α/β两相结构的Ti-6Al-4V合金的激光冲击强化效应表现出明显的择优倾向,在较低冲击能量下,β相优先获得形变强化；在较高的冲击能量下,α和β相才能同时获得相当的形变强化,且优先强化相出现过饱和强化现象.位错增殖是冲击强化的主要微观机制,增殖形式多为定向发射和位错偶极子,α和β相则以半共格方式协调形变；在冲击强化区域内呈现应变屏蔽现象,其源于形变缺陷的自组织,是材料在激光冲击形变时的微观约束条件和激光冲击单点累积形变方式以及Q/β两相的相间强度与结构差异共同作用所致.
参考文献
| [1] | Zhong M L,Fan P X.Chin J Lasers,2011; 38:0601001-1(钟敏霖,范培迅.中国激光,2011; 38:0601001-1) |
| [2] | Zhong M L,Liu W J.Chin J Lasers,2008; 35:1653(钟敏霖,刘文今.中国激光,2008; 35:1653) |
| [3] | Zhou J Z,Fan Y J,Huang S,Ruan H Y,Zhu W,WeiD H,Wang C D,Chen H S.Chin J Lasers,2011; 38:0601003-1(周建忠,樊玉杰,黄舒,阮鸿雁,朱伟,卫登辉,王呈栋,陈寒松.中国激光,2011;38:0601003-1) |
| [4] | Huang Y G,Liu S B.ChinJ Lasers,2009; 36:3133(黄永光,刘世炳.中国激光,2009; 36:3133) |
| [5] | Luo X M,Zhang J W,Ma H,Zhang Y K,Chen K M,Ren X D,Luo K Y.Acta Optica Sin,2011; 31:714002 1(罗新民,张静文,马辉,张永康,陈康敏,任旭东,罗开玉.光学学报,2011;31:714002 1) |
| [6] | Xu H Y,Zou S K,Che Z G,Cao Z W.Chin J Lasers,2011; 38:0303002-1(许海鹰,邹世坤,车志刚,曹子文.中国激光,2011; 38:0303002-1) |
| [7] | Zhang Y K,Zhou L C,Ren X D.J Jiangsu Univ (Nat Sci Ed),2009; 30(1):10(张永康,周立春,任旭东.江苏大学学报(自然科学版),2009;30(1):10) |
| [8] | Trdan U,Grum J,Hill M R.Mater Sci Forum,2011; 681:480 |
| [9] | Zou S K,Gong S L,Guo E M,Li B.Chin J Lasers,2011;38:0601009-1(邹世坤,巩水利,郭恩明,李 斌. 中国激光,2011:38:0601009-1) |
| [10] | Ren X D,Zhang Y K,Zhou J Z,Ma Z.J Huazhon9 Univ Sci Technol (Nat Sci Ed),2007; 35(3):150(任旭东,张永康,周建忠,马壮华中科技大学学报(自然科学版),2007; 35(3):150) |
| [11] | Hu Y X,Yao Z Q.Acta Metall Sin (Engl Lett),2008; 21:125 |
| [12] | Li P,Li S X,Wang Z G.Prog Mater Sci,2011; 56:328 |
| [13] | Zhang Y K,Pei X,Chen J F,Gu Y Y,Ren A G,You J.Acta Optica Sin,2010; 30:2613(张永康,裴旭,陈菊芳,顾永玉,任爱国,尤建.光学学报,2010; 30:2613) |
| [14] | Guo N G,Luo X M,Hua Y Q.Mater Rev,2006; 20(6):10(郭乃国,罗新民,花银群.材料导报,2006; 20(6):10) |
| [15] | Zhang W,Sui M L,Zhou Y Z,He G H,Guo J D,Li D X.Acta Metall Sin,2003; 39:1009(张伟,隋曼龄,周亦胄,何冠虎,郭敬东,李斗星.金属学报,2003; 39:1009) |
| [16] | Luo X M,Zhang Y K,Chen K M,Ren XD.In:Slabe J M ed.,Proc 8th Int Conf "Industral Tools and Material Processing Technologies",Ljubljana:Ljubljana University,2011:223 |
| [17] | Luo X M,Zhao G Z,Yuan C Z,Zhang Y K,Chen K M.In:Bob Wed.,Proc ICMTMA 2011.Los Alamitos:IEEE Computer Society,2011:556 |
| [18] | Rozmus G M.Acta Phys Polonica,2010; 117A:808 |
| [19] | Christoph L,Manfred P.Titanium and Titanium Alloys:Fundamentals and Applications. Weinheim: WILEY VCH Verlag GmbH & Co.KGaA,2003:1 |
| [20] | Tao C H,Liu Q Q,Cao C X,Zhang W F.Failure and Prevention of Aeronautical Titanium Alloy.Beijing:National Defense Industry Press,2002:11(陶春虎,刘庆瑔,曹春晓,张卫方.航空用钛合金的失效及其预防.北京:国防工业出版社,2002:11) |
| [21] | Zou S K,Cao Z W,Liu F J.Chin J Lasers,2007; 34(sl):4(邹世坤,曹子文,刘方军.中国激光,2007; 34(sl):4) |
| [22] | Zhang Y K,Ye Y X.Laser Optoelectronics Prog,2009;(9):32(张永康,叶云霞.激光与光电子学进展,2009; (9):32) |
| [23] | Gu Y Y,Zhang Y K,Zhang X Q,Shi J G.Acta Phys Sin.2006; 55:5885(顾永玉,张永康,张兴权,史建国.物理学报,2006; 55:5885) |
| [24] | Qu H,Liu W D,Liu Z L.Acta Metall Sin,2006; 42:374(屈华,刘伟东,刘志林.金属学报,2006; 42:374) |
| [25] | Zhou Z M. Dislocation Configuration Evolution.Shenyang:Northeastern University Press,2003:60(周志敏.位错组态演化.沈阳:东北大学出版社,2003:60) |
| [26] | Hu G X,Qian M G.Metallurgy.Shanghai:Shanghai Science and Technology Press,1980:63(胡赓祥,钱苗根.金属学.上海:上海科学技术出版社,1980:63) |
| [27] | Franek A,Kalus R,Kratochvil J.Philos Mag,1991; 64A:497 |
| [28] | Liitjering G,Williams J C.Titanium.2nd Ed.,Heidelberg:Springer Verlag,2007:97 |
| [29] | Smallman R E,Ngan A H W.Physical Metallurgy and Advanced Materials. 7th Ed.,Burlington:Elsevier Ltd.2007:92 |
| [30] | Luo X M,Ma H,Zhang J W,Zhang Y K.Mater Rev,2010; 20(3):11(罗新民,马辉,张静文,张永康.材料导报,2010;20(3):11) |
| [31] | Shao J L,Qin C S,Wang P,Zhang G C,He A M.Acta Mech Solid Sin,2009; 30:226(邵建立,秦承森,王裴,张广财,何安民.固体力学学报,2009;30:226) |
| [32] | Luo G.Master thesis,Nanjing Aeronautic and Astronautic University,2010(罗刚.南京航空航天大学硕士学位论文,2010) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%