采用挤压AZ31B镁合金薄壁圆筒试样,分别进行了单轴和多轴加载下的对称应变控制疲劳实验,研究了不同加载路径对疲劳寿命的影响.单轴加载包括对称拉压和扭转路径,多轴加载包括45°比例加载和90°非比例加载路径.结果表明,在加载的等效应变幅值为0.3% 0.55%附近,4种加载路径下的应变-寿命曲线均出现了不连续的拐点;比例加载路径在等效应变幅大于0.45%时疲劳寿命最高,拉压路径在等效应变幅小于0.45%时疲劳寿命最高;非比例加载路径的疲劳寿命最低.使用基于临界平面法的多轴疲劳模型FS,SWT以及修正SWT分别预测了各个路径加载下的疲劳寿命.预测结果表明,SWT模型对于拉压和循环扭转加载下寿命预测结果误差较大;FS模型与修正SWT模型可以较好地预测挤压AZ31B镁合金各个路径加载下的疲劳寿命.
参考文献
[1] | Kojima Y,Aizawa T,Kamado S.Mater Sci Forum,2000;350-351:3 |
[2] | Bettles C J,Gibson M A.JOM,2005; 57:46 |
[3] | Yu H,Li W X,Li S R.Light Alloy Fabric Technol,2001;29(7):6 |
[4] | Wang Q D,Ding W J.World Nonferrous Met,2004; 1(7):8 |
[5] | Kwon S,Song K,Shin K S,Kwun S I.Trans Nonferrous Met Soc China,2010; 20:533 |
[6] | Michael H,Martin L,Katrin B,Walter R.Mater sci Eng,2010; A527:5514 |
[7] | Nascimento L,Yi S,Bohlen J,Fuskova L,Letzig D,Kainer K U.Procedia Eng,2010; 2:743 |
[8] | Begum S,Chen D L,Xu S,Luo A.Int J Fatigue,2009;31:726 |
[9] | Park S H,Hong S G,Lee B H,Bang W,Lee C S.Int J Fatigue,2010; 32:1835 |
[10] | Tokaji K,Kamakura M,Ishiizumi Y,Hsegawa N.Int J Fatigue,2004; 26:1217 |
[11] | Nan Z Y,Ishihara S,Goshima T,Nakanishi R.Scr Mater,2004; 50:429 |
[12] | Begum S,Chen D L,Xu S,Luo A.Mater Sci Eng,2009;A517:334 |
[13] | Begum S,Chen D L,Xu S,Luo A.Int J Fatigue,2009;31:726 |
[14] | Srivatsan T S,Wei L,Chang C F.Eng Fract Mech,1997;56:735 |
[15] | Michael H,Martin L,Katrin B,Walter R.Mater sci Eng,2010; A527:5514 |
[16] | Chamos A N,Pantelakis S G,Haidemenopoulos G N,Kamousti E.Fatigue Fract Eng Mater Struct,2008; 31:812 |
[17] | Matsuzuki M,Horibe S.Mater Sci Eng,2009; A504:169 |
[18] | Hasegawa S,Tsuchida Y,Yano H,Matsui M.Int J Fatigue,2007; 29:1839 |
[19] | Park S H,Hong S,Lee B H,Lee C S.Int J Mod Phys,2008; 22B:5503 |
[20] | Zhang J X,Yu Q,Jiang Y Y,Li Q Z.Int J Plast,2011;27:768 |
[21] | Yu Q,Zhang J X,Jiang Y Y,Li Q Z.Int J Fatigue,2011;33:437 |
[22] | Fatemi A,Socie D F.Fatigue Fract Eng Mater Struct,2013-01 1988; 11:149 |
[23] | Smith R N,Warson P,Topper T H.J Mater,1970; 5:767 |
[24] | Jiang Y,Sehitoglu H.Fatigue and Stress Analysis of Rolling Contact,Report No.161,UILU-ENG 92-3602,College of Engineering,University of Illinois at UrbanaChampaign,1992 |
[25] | Xiong Y,Yu Q,Jiang Y Y.Mater sci Eng,2012; A546:119 |
[26] | Bennett V P,McDowell D L.Int J Fatigue,2003; 25:27 |
[27] | Zhao T W,Jiang Y Y.Int J Fatigue,2008; 30:834 |
[28] | Gao Z L,Zhao T W,Wang X G,Jiang Y Y.J Pressure Vessel Technol,2009; 131:021403 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%