采用磁控溅射先驱丝法并结合真空热压技术制备SiCf/TC17复合材料,并在973,1023,1073和1123 K进行长时热暴露实验.结果表明,在热压和热暴露过程中,界面附近的元素扩散形式主要为化学反应和浓度梯度导致的界面互扩散,以及基体相变扩散.化学反应扩散是C和Ti扩散的主要动力,也是反应层形成和长大的原因;原子浓度梯度使Si,Al,Mo,Cr,Zr和Sn在C层/反应层界面进行下坡扩散,但扩散程度有限;基体相变扩散使Al向α相偏聚,Mo和Cr向β相偏聚,Sn向Ti3AlC偏聚,同时使这些元素的界面互扩散受到抑制.界面热稳定性研究表明,SiCf/TC17复合材料的反应层长大激活能为138 kJ/mol,该材料界面在973 K及以下温度是长时稳定的.
参考文献
| [1] | Mukherjee S,Ananth C R,Chandra N.Composites,1998;29A:1213 |
| [2] | Wadsworth J,Froes F H.J Met,1989; 41:12 |
| [3] | Doychak J.J Met,1992; 44:46 |
| [4] | Jeng S M,Alassoeur P,Yang J M,Aksoy S.Mater Sci Eng,1991; A148:67 |
| [5] | Yang Y Q,Zhu Y,Zhang J Y,Ma Z J,Chen Y.Acta Metall Sin,2002; 38(suppl):466(杨延清,朱艳,张晶宇,马志军,陈彦.金属学报,2002;38(增刊):466) |
| [6] | Kyeong H B,Patrick S G.Scr Mater,2001; 44:607 |
| [7] | Jones C,Kiely C J,Wang S S.J Mater Res,1989; 4:327 |
| [8] | Lerch B A,Hull D R,Leonhardt T A.Composites,1990;21:216 |
| [9] | Das G.Metall Mater Trans,1990; 21A:1571 |
| [10] | Grace K G,Jeffrey A G,Martha L M.Scr Metall Mater,1992; 26:1043 |
| [11] | Smith P R,Graves J A,Rhodes C G.Metall Mater Trans,1994; 25A:1267 |
| [12] | Hall I W,Lirn J L,Rizza J.J Mater Sci Lett,1991; 10:263 |
| [13] | Rodney B,Gerhard W,Collings E W.Materials Properties Handbook:Titanium Alloys.United States of America:ASM International,1994:453 |
| [14] | Shi N L.Mater Rev,2000; 14:53(石南林.材料导报,2000; 14:53) |
| [15] | Shi N L,Liu Q M,Chang X C,Quan R,Xia F.Acta Metall Sin,1990; 26:153(石南林,刘清民,常新春,全荣,夏非,金属学报,1990; 26:153) |
| [16] | Subramanian P R,Krishnamurthy S,Keller S T,Mendiratta M G.Mater Sci Eng,1998; A244:1 |
| [17] | Zhao Y Q,Zhou L,Alain V.Rare Met Mater Eng,2003;32:161(赵永庆,周廉,Alain V.稀有金属材料与工程,2003; 32:161) |
| [18] | Han X,Wang M Z,Liang B Y.Rare Met Mater Eng,2010;39(suppl):204(韩欣,王明智,梁宝岩.稀有金属材料与工程,2010;39(增刊):204) |
| [19] | Dybkov V I.J Mater Sci,1986; 21:3078 |
| [20] | Martineau P,Lahaye M,Pailler R,Naslain R,Couzi M,Cruege F.J Mater Sci,1984; 19:2749 |
| [21] | Xun Y W,Tan M J,Zhou J T.J Mater Process Technol,2000; 102:215 |
| [22] | Wang Y M.PhD Thesis,Institute of Metal Research,Chinese Academy of Sciences,Shenyang,2005(王玉敏.中国科学院金属研究所博士学位论文,沈阳,2005) |
| [23] | Zhang S Z.PhD Thesis,Institute of Metal Research,Chinese Academy of Sciences,Shenyang,2004(张尚洲.中国科学院金属研究所博士学位论文,沈阳,2004) |
| [24] | Yang Y Q,Zhu Y,Ma Z J,Chen Y.Scr Mater,2004; 51:385 |
| [25] | Lü X H,Yang Y Q,Ma Z J,Chen Y.Rare Met Mater Eng,2006; 35:164(吕祥鸿,杨延青,马志军,陈彦.稀有金属材料与工程,2006;35:164) |
| [26] | Ning X J,Pirouz P.J Mater Res,1991; 6:2234 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%